METHOD OF OBTAINING FINE-CRYSTALLINE FERRITE-CHROMITES WITH SPINEL STRUCTURE
FIELD: chemical industry.SUBSTANCE: invention can be used in the chemical industry for the production of butadiene and the conversion of carbon monoxide (II). The method of obtaining fine-crystalline ferrite chromites with a spinel structure includes homogenizing the initial oxides of zinc (II), iron (III) and chromium (III). A mixture of oxides is obtained by the decomposition of solutions of zinc (II), iron (III) nitrates, chromium sulfate (III) with a concentration of 1 mol/L. A 10-20% ammonia solution with a concentration of 14 mol/L and a 25-35% citric acid solution with a concentration of 6.25 mol/L are introduced into the mixture of solutions with stirring. The resulting mixture is evaporated for 10-30 minutes. After that it is calcined for 10-20 minutes at 500-700°C until gas formation stops. Then heat treatment is carried out at 900°C for 30 minutes.EFFECT: invention makes it possible to simplify the heat treatment mode and reduce its duration, reduce the energy consumption when obtaining fine-crystalline zinc ferrite chromites, and increase the surface area of the material obtained.1 cl, 3 dwg, 1 tbl, 3 ex
Изобретение может быть использовано в химической промышленности при производстве бутадиена и конверсии оксида углерода (II). Способ получения мелкокристаллических ферритов-хромитов со структурой шпинели включает гомогенизацию исходных оксидов цинка (II), железа (III) и хрома (III). Смесь оксидов получают при разложении растворов нитратов цинка (II), железа (III), сульфата хрома (III) с концентрацией 1 моль/л. В смесь растворов вводят при перемешивании 10-20% раствора аммиака с концентрацией 14 моль/л и 25-35% раствора лимонной кислоты с концентрацией 6,25 моль/л. Полученную смесь выпаривают в течение 10-30 мин с последующим прокаливанием в течение 10-20 мин при 500-700°С до прекращения газообразования. Затем проводят термообработку при 900°С в течение 30 мин. Изобретение позволяет упростить режим термообработки и уменьшить её продолжительность, снизить энергоемкость при получении мелкокристаллических ферритов-хромитов цинка, увеличить площадь поверхности получаемого материала. 3 ил., 1 табл., 3 пр.
METHOD OF OBTAINING FINE-CRYSTALLINE FERRITE-CHROMITES WITH SPINEL STRUCTURE
FIELD: chemical industry.SUBSTANCE: invention can be used in the chemical industry for the production of butadiene and the conversion of carbon monoxide (II). The method of obtaining fine-crystalline ferrite chromites with a spinel structure includes homogenizing the initial oxides of zinc (II), iron (III) and chromium (III). A mixture of oxides is obtained by the decomposition of solutions of zinc (II), iron (III) nitrates, chromium sulfate (III) with a concentration of 1 mol/L. A 10-20% ammonia solution with a concentration of 14 mol/L and a 25-35% citric acid solution with a concentration of 6.25 mol/L are introduced into the mixture of solutions with stirring. The resulting mixture is evaporated for 10-30 minutes. After that it is calcined for 10-20 minutes at 500-700°C until gas formation stops. Then heat treatment is carried out at 900°C for 30 minutes.EFFECT: invention makes it possible to simplify the heat treatment mode and reduce its duration, reduce the energy consumption when obtaining fine-crystalline zinc ferrite chromites, and increase the surface area of the material obtained.1 cl, 3 dwg, 1 tbl, 3 ex
Изобретение может быть использовано в химической промышленности при производстве бутадиена и конверсии оксида углерода (II). Способ получения мелкокристаллических ферритов-хромитов со структурой шпинели включает гомогенизацию исходных оксидов цинка (II), железа (III) и хрома (III). Смесь оксидов получают при разложении растворов нитратов цинка (II), железа (III), сульфата хрома (III) с концентрацией 1 моль/л. В смесь растворов вводят при перемешивании 10-20% раствора аммиака с концентрацией 14 моль/л и 25-35% раствора лимонной кислоты с концентрацией 6,25 моль/л. Полученную смесь выпаривают в течение 10-30 мин с последующим прокаливанием в течение 10-20 мин при 500-700°С до прекращения газообразования. Затем проводят термообработку при 900°С в течение 30 мин. Изобретение позволяет упростить режим термообработки и уменьшить её продолжительность, снизить энергоемкость при получении мелкокристаллических ферритов-хромитов цинка, увеличить площадь поверхности получаемого материала. 3 ил., 1 табл., 3 пр.
METHOD OF OBTAINING FINE-CRYSTALLINE FERRITE-CHROMITES WITH SPINEL STRUCTURE
Способ получения мелкокристаллических ферритов-хромитов со структурой шпинели
SHABELSKAYA NINA PETROVNA (Autor:in) / EGOROVA MARINA ALEKSANDROVNA (Autor:in) / ARZUMANOVA ANNA VALEREVNA (Autor:in) / GAJDUKOVA YULIYA ALEKSANDROVNA (Autor:in) / VYALTSEV ALEKSANDR VLADIMIROVICH (Autor:in) / ZABABURIN VLADIMIR MIKHAJLOVICH (Autor:in) / LYASHENKO NADEZHDA VLADIMIROVNA (Autor:in)
29.04.2021
Patent
Elektronische Ressource
Russisch
IPC:
C01G
Verbindungen der von den Unterklassen C01D oder C01F nicht umfassten Metalle
,
COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
/
B01J
Chemische oder physikalische Verfahren, z.B. Katalyse oder Kolloidchemie
,
CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY
/
B82Y
Bestimmter Gebrauch oder bestimmte Anwendung von Nanostrukturen
,
SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES
/
C01B
NON-METALLIC ELEMENTS
,
Nichtmetallische Elemente
/
C04B
Kalk
,
LIME
/
C30B
SINGLE-CRYSTAL GROWTH
,
Züchten von Einkristallen
Thermal Expansion of Chromites and Zinc Spinel
| British Library Online Contents | 1999
Soft magnetic ferrite with spinel structure and application thereof
| Europäisches Patentamt | 2024
| Europäisches Patentamt | 2021
Crystal Structure Refinement of the Mechanically Activated Spinel-Ferrite
| British Library Online Contents | 1996
Bulk and surface structure characterization of nanoscopic silver doped lanthanum chromites
| British Library Online Contents | 2013