METHOD FOR MANUFACTURING A COMPOSITE BARIUM TITANATE - BARIUM FERRITE IN ALUMINUM-CONTAINING CRUCIBLES
FIELD: composite barium titanate production.SUBSTANCE: method of manufacturing a composite barium titanate - barium ferrite refers to the production of ferroelectric materials or multiferroics. To implement the proposed method, separate grinding of barium titanate and barium ferrite to a fineness of 10 microns is performed. The obtained powders of barium titanate and barium ferrite are mixed in a 4:1 ratio and mixed until homogeneous. To the resulting mixture is added 5 wt.% of a five percent by weight aqueous solution of polyvinyl alcohol as a plasticizer and stirring is carried out until homogeneous. The resulting mixture is cold formed with a pressure of 600 MPa. The composite is synthesized at 1248-1250°C for 2-6 hours, followed by smooth cooling of the resulting composite for 8-20 hours.EFFECT: creation of a composite multiferroic with the required magnetoelectric properties at a minimum sintering temperature.1 cl, 1 dwg
Способ изготовления композита титанат бария - феррит бария относится к производству сегнетомагнитных материалов или мультиферроиков. Для осуществления заявляемого способа производится раздельный размол титаната бария и феррита бария до дисперсности 10 мкм. Полученные порошки титаната бария и феррита бария смешивают в пропорции 4:1 и перемешивают до однородности. К полученной смеси добавляют 5 масс.% пятипроцентного по массе водного раствора поливинилового спирта в качестве пластификатора и осуществляют перемешивание до однородности. Производят холодную формовку полученной смеси давлением 600 МПа. Производится синтез композита при 1248-1250°C в течение 2-6 ч с последующим плавным остыванием полученного композита в течение 8-20 ч. Технический результат изобретения – создание композитного мультиферроика с требуемыми магнитоэлектрическими свойствами при минимальной температуре спекания. 1 ил.
METHOD FOR MANUFACTURING A COMPOSITE BARIUM TITANATE - BARIUM FERRITE IN ALUMINUM-CONTAINING CRUCIBLES
FIELD: composite barium titanate production.SUBSTANCE: method of manufacturing a composite barium titanate - barium ferrite refers to the production of ferroelectric materials or multiferroics. To implement the proposed method, separate grinding of barium titanate and barium ferrite to a fineness of 10 microns is performed. The obtained powders of barium titanate and barium ferrite are mixed in a 4:1 ratio and mixed until homogeneous. To the resulting mixture is added 5 wt.% of a five percent by weight aqueous solution of polyvinyl alcohol as a plasticizer and stirring is carried out until homogeneous. The resulting mixture is cold formed with a pressure of 600 MPa. The composite is synthesized at 1248-1250°C for 2-6 hours, followed by smooth cooling of the resulting composite for 8-20 hours.EFFECT: creation of a composite multiferroic with the required magnetoelectric properties at a minimum sintering temperature.1 cl, 1 dwg
Способ изготовления композита титанат бария - феррит бария относится к производству сегнетомагнитных материалов или мультиферроиков. Для осуществления заявляемого способа производится раздельный размол титаната бария и феррита бария до дисперсности 10 мкм. Полученные порошки титаната бария и феррита бария смешивают в пропорции 4:1 и перемешивают до однородности. К полученной смеси добавляют 5 масс.% пятипроцентного по массе водного раствора поливинилового спирта в качестве пластификатора и осуществляют перемешивание до однородности. Производят холодную формовку полученной смеси давлением 600 МПа. Производится синтез композита при 1248-1250°C в течение 2-6 ч с последующим плавным остыванием полученного композита в течение 8-20 ч. Технический результат изобретения – создание композитного мультиферроика с требуемыми магнитоэлектрическими свойствами при минимальной температуре спекания. 1 ил.
METHOD FOR MANUFACTURING A COMPOSITE BARIUM TITANATE - BARIUM FERRITE IN ALUMINUM-CONTAINING CRUCIBLES
Способ изготовления композита титанат бария - феррит бария в алюминийсодержащих тиглях
SHISHKOV GRIGORII SERGEEVICH (Autor:in) / MALYSHKINA OLGA VITALEVNA (Autor:in)
13.12.2021
Patent
Elektronische Ressource
Russisch
IPC:
C04B
Kalk
,
LIME
Manufacturing Method of Barium Titanate and Barium Titanate fabricated thereby
Europäisches Patentamt | 2017
Method of manufacturing barium titanate and electronic component of barium titanate
| Europäisches Patentamt | 2017
Preparation method of bismuth ferrite-barium titanate composite piezoelectric ceramic
| Europäisches Patentamt | 2020
BARIUM TITANATE THIN FILM AND BARIUM TITANATE THIN FILM MANUFACTURING METHOD
Europäisches Patentamt | 2017
| Europäisches Patentamt | 2023