METHOD FOR MAKING RADIOTRANSPARENT CERAMIC HOUSING FOR LIGHTING FIXTURE, RADIOTRANSPARENT CERAMIC HOUSING FOR LIGHTING FIXTURE
FIELD: physics.SUBSTANCE: invention relates to production of ceramic articles. Disclosed is a method of making a ceramic radiotransparent housing for a lighting device, according to which Shulepovskaya clay is pre-mixed, potassium feldspar kaolin, chamotte, diopside, bentonite to obtain a mass with moisture content of 19.0–21.0 %, which is then held in tight conditions for 12 hours and subjected to a vacuumizing process on a vacuum press and moulded at pressure of 1.5–10 MPa to produce a workpiece. Obtained workpieces are dried for 40–60 minutes at temperature of 150–170 °C and glazing by applying electrotechnical glaze on the workpiece body by sputtering with a glaze layer thickness of 0.3–0.5 mm, glazed articles are fired, after firing the articles are cut to produce a ceramic body for a lighting fixture. Crude mixture contains components in the following ratio, wt. %: Shulepovskaya clay 34.0–37.0, potassium feldspar kaolin 37.0–42.2, chamotte 7.0–11.0, diopside 10.0–13.0, bentonite 1.0–2.0.EFFECT: technical result of the invention is the manufacture of a radiotransparent ceramic housing for the lighting device, which provides effective protection of the power supply and the radio transmitting device.4 cl, 1 ex
Изобретение относится к области производства керамических изделий. Предложен способ изготовления керамического радиопрозрачного корпуса для осветительного прибора, согласно которому предварительно смешивают глину Шулеповскую, калиевый полевошпатный каолин, шамот, диопсид, бентонит с получением массы влажностью 19,0-21,0%, которую затем выдерживают в герметичных условиях в течение 12 часов и подвергают процессу вакуумирования на вакуум-прессе и формуют под давлением 1,5-10 МПа с получением заготовки изделия. Полученные заготовки сушат в течение 40-60 минут при температуре 150-170°С и глазуруют путем нанесения электротехнической глазури на корпус заготовки методом напыления с толщиной слоя глазури 0,3-0,5 мм, глазурованные изделия подвергают обжигу, после обжига изделия нарезают с получением керамического корпуса для осветительного прибора. Сырьевая смесь содержит компоненты в следующем соотношении, мас.%: глина Шулеповская 34,0-37,0, калиевый полевошпатный каолин 37,0-42,2, шамот 7,0-11,0, диопсид 10,0-13,0, бентонит 1,0-2,0. Технический результат изобретения - изготовление радиопрозрачного керамического корпуса для осветительного прибора, который обеспечивает эффективную защиту источника питания и радиопередающего устройства. 2 н. и 2 з.п. ф-лы, 1 пр.
METHOD FOR MAKING RADIOTRANSPARENT CERAMIC HOUSING FOR LIGHTING FIXTURE, RADIOTRANSPARENT CERAMIC HOUSING FOR LIGHTING FIXTURE
FIELD: physics.SUBSTANCE: invention relates to production of ceramic articles. Disclosed is a method of making a ceramic radiotransparent housing for a lighting device, according to which Shulepovskaya clay is pre-mixed, potassium feldspar kaolin, chamotte, diopside, bentonite to obtain a mass with moisture content of 19.0–21.0 %, which is then held in tight conditions for 12 hours and subjected to a vacuumizing process on a vacuum press and moulded at pressure of 1.5–10 MPa to produce a workpiece. Obtained workpieces are dried for 40–60 minutes at temperature of 150–170 °C and glazing by applying electrotechnical glaze on the workpiece body by sputtering with a glaze layer thickness of 0.3–0.5 mm, glazed articles are fired, after firing the articles are cut to produce a ceramic body for a lighting fixture. Crude mixture contains components in the following ratio, wt. %: Shulepovskaya clay 34.0–37.0, potassium feldspar kaolin 37.0–42.2, chamotte 7.0–11.0, diopside 10.0–13.0, bentonite 1.0–2.0.EFFECT: technical result of the invention is the manufacture of a radiotransparent ceramic housing for the lighting device, which provides effective protection of the power supply and the radio transmitting device.4 cl, 1 ex
Изобретение относится к области производства керамических изделий. Предложен способ изготовления керамического радиопрозрачного корпуса для осветительного прибора, согласно которому предварительно смешивают глину Шулеповскую, калиевый полевошпатный каолин, шамот, диопсид, бентонит с получением массы влажностью 19,0-21,0%, которую затем выдерживают в герметичных условиях в течение 12 часов и подвергают процессу вакуумирования на вакуум-прессе и формуют под давлением 1,5-10 МПа с получением заготовки изделия. Полученные заготовки сушат в течение 40-60 минут при температуре 150-170°С и глазуруют путем нанесения электротехнической глазури на корпус заготовки методом напыления с толщиной слоя глазури 0,3-0,5 мм, глазурованные изделия подвергают обжигу, после обжига изделия нарезают с получением керамического корпуса для осветительного прибора. Сырьевая смесь содержит компоненты в следующем соотношении, мас.%: глина Шулеповская 34,0-37,0, калиевый полевошпатный каолин 37,0-42,2, шамот 7,0-11,0, диопсид 10,0-13,0, бентонит 1,0-2,0. Технический результат изобретения - изготовление радиопрозрачного керамического корпуса для осветительного прибора, который обеспечивает эффективную защиту источника питания и радиопередающего устройства. 2 н. и 2 з.п. ф-лы, 1 пр.
METHOD FOR MAKING RADIOTRANSPARENT CERAMIC HOUSING FOR LIGHTING FIXTURE, RADIOTRANSPARENT CERAMIC HOUSING FOR LIGHTING FIXTURE
Способ изготовления радиопрозрачного керамического корпуса для осветительного прибора, радиопрозрачный керамический корпус для осветительного прибора