COMPOSITION FOR COLORING SURFACE OF CONCRETE
A composition for coloring the surface of concrete, according to the present invention, comprises: 8 wt% of a coloring dye having a size of 0.01-1 nm; 45 wt% of a diluent formed by mixing ion exchange water and ethylene glycol in a ratio of 7:3 by weight; 7 wt% of methyl methacrylate; 0.06 wt% of polydimethylsiloxane; 0.5 wt% of a fluoropolymer; 6 wt% of colloidal silica; and 25 wt% a modified silicate. According to the present invention, the pH of a surface-colored part is 11-13, which is as alkaline as the concrete of an alkaline component having a hydroxyl group of Ca(OH)3, and a firm and beautiful concrete surface is completed since the coloring thereof is carried out by penetrating 2-3 mm. In addition, semi-permanent durability is provided to the surface of concrete while simultaneously enabling stable color expression, and there are no agglomeration of a preparation or no two colors, and no spots or development phenomena during coloring.
Selon la présente invention, une composition destinée à la coloration de la surface d'un béton comprend : 8 % en poids d'une teinture colorante présentant une taille de 0,01 à 1 nm; 45 % en poids d'un diluant formé en mélangeant de l'eau pour l'échange d'ions et de l'éthylène glycol en une proportion de 7:3 en poids; 7 % en poids de méthacrylate de méthyle; 0,06 % en poids de polydiméthylsiloxane; 0,5 % en poids d'un fluoropolymère; 6 % en poids de silice colloïdale; et 25 % en poids d'un silicate modifié. Selon la présente invention, le pH d'une partie colorée en surface est de 11 à 13, ce qui est aussi alcalin que le béton d'un constituant alcalin comprenant un groupe hydroxyle de Ca(OH)3. En outre, une belle et solide surface de béton est obtenue, la coloration de celle-ci s'effectuant par pénétration sur 2 à 3 mm. De plus, la surface du béton présente une durabilité semi-permanente tout en permettant simultanément l'expression d'une couleur stable, et l'on n'observe aucune agglomération d'une préparation ni la présence de deux couleurs, ni l'apparition de points ou de phénomènes de développement au cours de la coloration.
본 발명에 따른 콘크리트 표면 착색 조성물은, 0.01~1 nm 크기의 착색용 염료 8 wt%, 이온교환수와 에틸렌글리콜을 7:3 중량비로 혼합하여 이루어진 희석제 45 wt%, 메타크릴산메틸에스테르 7 wt%, 폴리디메틸실록산 0.06 wt%, 플루오르폴리머 0.5 wt%, 콜로이달실리카 6 wt%, 변성실리케이트 25 wt%를 포함하여 이루어지는 것을 특징으로 한다.본 발명에 의하면, 표면 착색된 부분의 PH가 11~13으로서 Ca[OH]3수산기를 가진 알칼리 성분의 콘크리트와 같은 알칼리성을 가지며, 2~3mm의 침투에 의한 착색이 이루어져 견고하면서 미려한 콘크리트 표면이 완성된다. 또한, 콘크리트 표면에 반영구적인 내구력이 부여됨과 동시에 안정적인 색상발현이 이루어지며, 제재의 뭉침이나 이색과 착색 시 얼룩이나 발색현상이 발생되지 않는다.
COMPOSITION FOR COLORING SURFACE OF CONCRETE
A composition for coloring the surface of concrete, according to the present invention, comprises: 8 wt% of a coloring dye having a size of 0.01-1 nm; 45 wt% of a diluent formed by mixing ion exchange water and ethylene glycol in a ratio of 7:3 by weight; 7 wt% of methyl methacrylate; 0.06 wt% of polydimethylsiloxane; 0.5 wt% of a fluoropolymer; 6 wt% of colloidal silica; and 25 wt% a modified silicate. According to the present invention, the pH of a surface-colored part is 11-13, which is as alkaline as the concrete of an alkaline component having a hydroxyl group of Ca(OH)3, and a firm and beautiful concrete surface is completed since the coloring thereof is carried out by penetrating 2-3 mm. In addition, semi-permanent durability is provided to the surface of concrete while simultaneously enabling stable color expression, and there are no agglomeration of a preparation or no two colors, and no spots or development phenomena during coloring.
Selon la présente invention, une composition destinée à la coloration de la surface d'un béton comprend : 8 % en poids d'une teinture colorante présentant une taille de 0,01 à 1 nm; 45 % en poids d'un diluant formé en mélangeant de l'eau pour l'échange d'ions et de l'éthylène glycol en une proportion de 7:3 en poids; 7 % en poids de méthacrylate de méthyle; 0,06 % en poids de polydiméthylsiloxane; 0,5 % en poids d'un fluoropolymère; 6 % en poids de silice colloïdale; et 25 % en poids d'un silicate modifié. Selon la présente invention, le pH d'une partie colorée en surface est de 11 à 13, ce qui est aussi alcalin que le béton d'un constituant alcalin comprenant un groupe hydroxyle de Ca(OH)3. En outre, une belle et solide surface de béton est obtenue, la coloration de celle-ci s'effectuant par pénétration sur 2 à 3 mm. De plus, la surface du béton présente une durabilité semi-permanente tout en permettant simultanément l'expression d'une couleur stable, et l'on n'observe aucune agglomération d'une préparation ni la présence de deux couleurs, ni l'apparition de points ou de phénomènes de développement au cours de la coloration.
본 발명에 따른 콘크리트 표면 착색 조성물은, 0.01~1 nm 크기의 착색용 염료 8 wt%, 이온교환수와 에틸렌글리콜을 7:3 중량비로 혼합하여 이루어진 희석제 45 wt%, 메타크릴산메틸에스테르 7 wt%, 폴리디메틸실록산 0.06 wt%, 플루오르폴리머 0.5 wt%, 콜로이달실리카 6 wt%, 변성실리케이트 25 wt%를 포함하여 이루어지는 것을 특징으로 한다.본 발명에 의하면, 표면 착색된 부분의 PH가 11~13으로서 Ca[OH]3수산기를 가진 알칼리 성분의 콘크리트와 같은 알칼리성을 가지며, 2~3mm의 침투에 의한 착색이 이루어져 견고하면서 미려한 콘크리트 표면이 완성된다. 또한, 콘크리트 표면에 반영구적인 내구력이 부여됨과 동시에 안정적인 색상발현이 이루어지며, 제재의 뭉침이나 이색과 착색 시 얼룩이나 발색현상이 발생되지 않는다.
COMPOSITION FOR COLORING SURFACE OF CONCRETE
COMPOSITION POUR LA COLORATION D'UNE SURFACE DE BÉTON
콘크리트 표면 착색 조성물
KIM DONGGYU (Autor:in)
03.12.2015
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
| Europäisches Patentamt | 2024
CONCRETE COLORING AGENT, CONCRETE COLORING METHOD AND CONCRETE
| Europäisches Patentamt | 2015
| British Library Online Contents | 2000