METHOD FOR PRODUCING A CARBONATE BONDED, PRESS-MOULDED ARTICLE
The carbonate bonded, press-moulded article is produced by press-moulding a particulate, carbonatable material that contains water and by carbonating the obtained compact with carbon dioxide gas. In order to be able to ensure an optimal compressive strength of the article two types of tests are provided. In the first type of test a sample of the particulate material is compressed with an increasing compaction pressure and when water starts to be expelled from the material as from a particular compaction pressure, the press-moulding step is performed with a compaction pressure which is at least 7 MPa smaller than this compaction pressure. In the second type of test different samples of the particulate material are press-moulded with different compaction pressures and, after having released the compaction pressure, the density of the compact is determined. In case this density decreases instead of increases as from a particular compaction pressure, the press- moulding step is performed with a compaction pressure which is smaller than this particular compaction pressure.
Selon l'invention, un article moulé à la presse lié par du carbonate est produit par moulage à la presse d'un matériau particulaire pouvant être carbonaté qui contient de l'eau et par carbonatation du comprimé obtenu avec du dioxyde de carbone gazeux. Afin de pouvoir garantir une résistance à la compression optimale de l'article, deux types d'essai sont utilisés. Dans le premier type d'essai, un échantillon de la matière particulaire est comprimé avec une pression de compactage croissante et ensuite lorsque de l'eau commence se dégager de la matière à partir d'une pression de compactage particulière, l'étape de moulage à la presse est effectuée avec une pression de compactage qui est au moins 7 MPa plus petite que cette pression de compactage. Dans le second type d'essai, différents échantillons de la matière particulaire sont moulés à la presse avec différentes pressions de compactage et, après relâchement de la pression de compactage, la masse volumique du comprimé est déterminé. Dans le cas où cette masse volumique diminue au lieu d'augmenter à partir d'une pression de compactage particulière, l'étape de moulage à la presse est effectuée avec une pression de compactage qui est plus petite que cette pression de compactage particulière.
METHOD FOR PRODUCING A CARBONATE BONDED, PRESS-MOULDED ARTICLE
The carbonate bonded, press-moulded article is produced by press-moulding a particulate, carbonatable material that contains water and by carbonating the obtained compact with carbon dioxide gas. In order to be able to ensure an optimal compressive strength of the article two types of tests are provided. In the first type of test a sample of the particulate material is compressed with an increasing compaction pressure and when water starts to be expelled from the material as from a particular compaction pressure, the press-moulding step is performed with a compaction pressure which is at least 7 MPa smaller than this compaction pressure. In the second type of test different samples of the particulate material are press-moulded with different compaction pressures and, after having released the compaction pressure, the density of the compact is determined. In case this density decreases instead of increases as from a particular compaction pressure, the press- moulding step is performed with a compaction pressure which is smaller than this particular compaction pressure.
Selon l'invention, un article moulé à la presse lié par du carbonate est produit par moulage à la presse d'un matériau particulaire pouvant être carbonaté qui contient de l'eau et par carbonatation du comprimé obtenu avec du dioxyde de carbone gazeux. Afin de pouvoir garantir une résistance à la compression optimale de l'article, deux types d'essai sont utilisés. Dans le premier type d'essai, un échantillon de la matière particulaire est comprimé avec une pression de compactage croissante et ensuite lorsque de l'eau commence se dégager de la matière à partir d'une pression de compactage particulière, l'étape de moulage à la presse est effectuée avec une pression de compactage qui est au moins 7 MPa plus petite que cette pression de compactage. Dans le second type d'essai, différents échantillons de la matière particulaire sont moulés à la presse avec différentes pressions de compactage et, après relâchement de la pression de compactage, la masse volumique du comprimé est déterminé. Dans le cas où cette masse volumique diminue au lieu d'augmenter à partir d'une pression de compactage particulière, l'étape de moulage à la presse est effectuée avec une pression de compactage qui est plus petite que cette pression de compactage particulière.
METHOD FOR PRODUCING A CARBONATE BONDED, PRESS-MOULDED ARTICLE
PROCÉDÉ PERMETTANT LA PRODUCTION D'UN ARTICLE MOULÉ À LA PRESSE LIÉ PAR DU CARBONATE
MAYELLE NICK (Autor:in) / BOUILLOT FRÉDÉRIQUE (Autor:in) / VAN MECHELEN DIRK (Autor:in)
03.03.2016
Patent
Elektronische Ressource
Englisch
METHOD FOR PRODUCING A CARBONATE BONDED, PRESS-MOULDED ARTICLE
| Europäisches Patentamt | 2017
Method for producing a carbonate bonded, press-moulded article
| Europäisches Patentamt | 2016
Method for producing a carbonate bonded, press-moulded article
| Europäisches Patentamt | 2020
Method for producing a carbonate bonded, press-moulded article
| Europäisches Patentamt | 2019
METHOD FOR PRODUCING A CARBONATE BONDED, PRESS-MOULDED ARTICLE
| Europäisches Patentamt | 2018