TRANSLUCENT ZIRCONIA SINTERED BODY, METHOD FOR MANUFACTURING SAME, AND USE THEREOF
Provided is a zirconia sintered body having both high translucency and high strength. This zirconia sintered body is characterized by including crystal grains that include a cubic crystal domain and a tetragonal crystal domain, and by a stabilizer and lanthanum being dissolved therein. This sintered body can be obtained by a manufacturing method characterized in comprising: a mixing step of mixing a zirconia source material, stabilizer source material, and lanthanum source material to obtain a mixed powder; a molding step of molding the obtained mixed powder to obtain a molded body; a sintering step of sintering the obtained molded body at a sintering temperature of 1650°C or higher to obtain a sintered body; and a temperature reducing step of reducing the temperature from the sintering temperature to 1000°C at a temperature reducing speed of over 1°C/min.
Cette invention concerne un corps fritté en zircone ayant à la fois une translucidité élevée et une résistance élevée. Le corps fritté en zircone selon l'invention est caractérisé en ce qu'il contient des grains cristallins à domaine cristallin cubique et à domaine cristallin tétragonal, ainsi qu'un stabilisant et du lanthane à l'état dissous. Le corps fritté peut être obtenu par un procédé de fabrication caractérisé en ce qu'il comprend : une étape de mélange consistant à mélanger une matière source de zircone, une matière source de stabilisant, et une matière source de lanthane pour obtenir un mélange de poudres ; une étape de moulage consistant à mouler le mélange de poudres obtenu pour obtenir un corps moulé ; une étape de frittage consistant à fritter le corps moulé obtenu à une température de frittage de 1650°C ou plus pour obtenir un corps fritté ; et une étape de réduction de température consistant à réduire la température de la température de frittage à 1000°C à une vitesse de réduction de température de plus de 1°C/min.
高い透光性及び高い強度を兼備したジルコニア焼結体を提供する。立方晶ドメイン及び正方晶ドメインを含む結晶粒子を含み、安定化剤及びランタンを固溶することを特徴とするジルコニア焼結体。このような焼結体はジルコニア原料、安定化剤原料及びランタン原料を混合して混合粉末を得る混合工程、得られた混合粉末を成形して成形体を得る成形工程、得られた成形体を１６５０℃以上の焼結温度で焼結して焼結体を得る焼結工程、及び、焼結温度から１０００℃までを１℃／ｍｉｎ超の降温速度で降温する降温工程、を含むことを特徴とする製造方法により得ることができる。
TRANSLUCENT ZIRCONIA SINTERED BODY, METHOD FOR MANUFACTURING SAME, AND USE THEREOF
Provided is a zirconia sintered body having both high translucency and high strength. This zirconia sintered body is characterized by including crystal grains that include a cubic crystal domain and a tetragonal crystal domain, and by a stabilizer and lanthanum being dissolved therein. This sintered body can be obtained by a manufacturing method characterized in comprising: a mixing step of mixing a zirconia source material, stabilizer source material, and lanthanum source material to obtain a mixed powder; a molding step of molding the obtained mixed powder to obtain a molded body; a sintering step of sintering the obtained molded body at a sintering temperature of 1650°C or higher to obtain a sintered body; and a temperature reducing step of reducing the temperature from the sintering temperature to 1000°C at a temperature reducing speed of over 1°C/min.
Cette invention concerne un corps fritté en zircone ayant à la fois une translucidité élevée et une résistance élevée. Le corps fritté en zircone selon l'invention est caractérisé en ce qu'il contient des grains cristallins à domaine cristallin cubique et à domaine cristallin tétragonal, ainsi qu'un stabilisant et du lanthane à l'état dissous. Le corps fritté peut être obtenu par un procédé de fabrication caractérisé en ce qu'il comprend : une étape de mélange consistant à mélanger une matière source de zircone, une matière source de stabilisant, et une matière source de lanthane pour obtenir un mélange de poudres ; une étape de moulage consistant à mouler le mélange de poudres obtenu pour obtenir un corps moulé ; une étape de frittage consistant à fritter le corps moulé obtenu à une température de frittage de 1650°C ou plus pour obtenir un corps fritté ; et une étape de réduction de température consistant à réduire la température de la température de frittage à 1000°C à une vitesse de réduction de température de plus de 1°C/min.
高い透光性及び高い強度を兼備したジルコニア焼結体を提供する。立方晶ドメイン及び正方晶ドメインを含む結晶粒子を含み、安定化剤及びランタンを固溶することを特徴とするジルコニア焼結体。このような焼結体はジルコニア原料、安定化剤原料及びランタン原料を混合して混合粉末を得る混合工程、得られた混合粉末を成形して成形体を得る成形工程、得られた成形体を１６５０℃以上の焼結温度で焼結して焼結体を得る焼結工程、及び、焼結温度から１０００℃までを１℃／ｍｉｎ超の降温速度で降温する降温工程、を含むことを特徴とする製造方法により得ることができる。
TRANSLUCENT ZIRCONIA SINTERED BODY, METHOD FOR MANUFACTURING SAME, AND USE THEREOF
CORPS FRITTÉ EN ZIRCONE TRANSLUCIDE, SON PROCÉDÉ DE FABRICATION ET UTILISATION
透光性ジルコニア焼結体及びその製造方法並びにその用途
YAMASHITA ISAO (Autor:in) / MACHIDA YUYA (Autor:in)
21.07.2016
Patent
Elektronische Ressource
Japanisch
TRANSLUCENT ZIRCONIA SINTERED BODY, METHOD FOR MANUFACTURING SAME, AND USE THEREOF
| Europäisches Patentamt | 2017
TRANSLUCENT ZIRCONIA SINTERED BODY, METHOD FOR MANUFACTURING SAME, AND USE THEREOF
| Europäisches Patentamt | 2020
Translucent zirconia sintered body, method for manufacturing same, and use thereof
| Europäisches Patentamt | 2019
TRANSLUCENT ZIRCONIA SINTERED BODY AND MANUFACTURING METHOD THEREOF AND APPLICATION THEREOF
| Europäisches Patentamt | 2017
COLORED TRANSLUCENT ZIRCONIA SINTERED BODY AND USE THEREOF
| Europäisches Patentamt | 2021