METHOD FOR PRODUCING FUNCTIONAL COMPOSITION BENEFICIAL TO HUMAN BODY
The present invention relates to a method for producing a functional composition beneficial to the human body. Specific steps thereof are as follows: a ferrite blending step (S110) in which 45-55 wt% of ferric oxide, 12-16 wt% of nickel oxide, 14-18 wt% of zinc oxide, 4-6 wt% of copper oxide, 4-8 wt% of lithium, 4-8 wt% of barium and 2-4 wt% of magnesium are mixed so as to prepare a ferrite mixed raw material; a ferrite raw material suspending step (S120 ) in which 130-170 wt% of water with respect to the weight of the mixed raw material, 2-4 wt% of a dispersant with respect to the weight of the mixed raw material, and 2-3 wt% of a binder with respect to the weight of the mixed raw material are inserted so as to prepare a mixture in a suspension state; a ferrite raw material granulation step (S130) for spray-drying the mixture in a suspension state so as to granulate the mixture; a heat treatment sintering step (S140) for heating the granular ferrite material at a temperature of 1,000-1,400℃ for 3-8 hours so as to sinter a ferrite sintered body; and a ferrite sintered body pulverization step (S150) for pulverizing the heat-treated ferrite sintered body into powder.
La présente invention concerne un procédé de production d'une composition fonctionnelle bénéfique pour le corps humain. Les étapes spécifiques de ce dernier sont comme suit : une étape de mélange de ferrite (S110) dans laquelle 45 à 55 % en poids d'oxyde ferrique, 12 à 16 % en poids d'oxyde de nickel, 14 à 18 % en poids d'oxyde de zinc, 4 à 6 % en poids d'oxyde de cuivre, 4 à 8 % en poids de lithium, 4 à 8 % en poids de baryum et 2 à 4 % en poids de magnésium sont mélangés de manière à préparer une matière première à base de ferrite mélangée; une étape de mise en suspension de la matière première à base de ferrite (S120) dans laquelle, 130 à 170 % en poids d'eau par rapport au poids de la matière première mélangée, 2 à 4 % en poids d'un dispersant par rapport au poids de la matière première mélangée, et 2 à 3 % en poids d'un liant par rapport au poids de la matière première mélangée sont insérés de manière à préparer un mélange à l'état de suspension; une étape de granulation de matière première à base de ferrite (S130) pour sécher par pulvérisation le mélange à l'état de suspension de manière à granuler le mélange; une étape de frittage par traitement thermique (S140) pour chauffer le matériau de ferrite granulaire à une température de 1 000 à 1 400 °C pendant 3 à 8 heures de sorte à fritter un corps fritté en ferrite; et une étape de pulvérisation de corps fritté en ferrite (S150) pour pulvériser le corps fritté en ferrite traité thermiquement en une poudre.
본 발명은 인체에 유익한 기능성 조성물의 제조방법이다. 그 구체적인 공정은 다음과 같다. 산화제2철 45~55중량%, 산화니켈 12~16중량%, 산화아연 14~18중량%, 산화구리 4~6중량%, 리튬 4~8중량%, 바륨 4~8중량% 및 마그네슘 2~4중량%를 혼합하여 페라이트 혼합원료를 조성하는 페라이트 배합공정(S110)과; 상기 혼합원료의 무게에 대하여 물 130~170중량%, 분산제는 혼합원료의 무게에 대하여 2~4중량%, 결착제는 혼합원료의 무게에 대하여 2~3중량%를 투입하여 현탁액 상태의 혼합물로 만드는 페라이트원료의 현탁화 공정(S120)과; 상기 현탁액 상태의 혼합물을 분무 건조하여 과립상으로 만드는 페라이트원료 과립화 공정(S130)과; 과립상의 페라이트원료를 3~8시간 동안 1,000~1,400℃ 온도로 가열하여 페라이트소결체(Ferrite)를 소성하는 열처리 소결공정(S140)과; 상기 열처리된 페라이트소결체를 분말로 분쇄하는 페라이트소결체 분말공정(S150)을 포함하여 이루어진다.
METHOD FOR PRODUCING FUNCTIONAL COMPOSITION BENEFICIAL TO HUMAN BODY
The present invention relates to a method for producing a functional composition beneficial to the human body. Specific steps thereof are as follows: a ferrite blending step (S110) in which 45-55 wt% of ferric oxide, 12-16 wt% of nickel oxide, 14-18 wt% of zinc oxide, 4-6 wt% of copper oxide, 4-8 wt% of lithium, 4-8 wt% of barium and 2-4 wt% of magnesium are mixed so as to prepare a ferrite mixed raw material; a ferrite raw material suspending step (S120 ) in which 130-170 wt% of water with respect to the weight of the mixed raw material, 2-4 wt% of a dispersant with respect to the weight of the mixed raw material, and 2-3 wt% of a binder with respect to the weight of the mixed raw material are inserted so as to prepare a mixture in a suspension state; a ferrite raw material granulation step (S130) for spray-drying the mixture in a suspension state so as to granulate the mixture; a heat treatment sintering step (S140) for heating the granular ferrite material at a temperature of 1,000-1,400℃ for 3-8 hours so as to sinter a ferrite sintered body; and a ferrite sintered body pulverization step (S150) for pulverizing the heat-treated ferrite sintered body into powder.
La présente invention concerne un procédé de production d'une composition fonctionnelle bénéfique pour le corps humain. Les étapes spécifiques de ce dernier sont comme suit : une étape de mélange de ferrite (S110) dans laquelle 45 à 55 % en poids d'oxyde ferrique, 12 à 16 % en poids d'oxyde de nickel, 14 à 18 % en poids d'oxyde de zinc, 4 à 6 % en poids d'oxyde de cuivre, 4 à 8 % en poids de lithium, 4 à 8 % en poids de baryum et 2 à 4 % en poids de magnésium sont mélangés de manière à préparer une matière première à base de ferrite mélangée; une étape de mise en suspension de la matière première à base de ferrite (S120) dans laquelle, 130 à 170 % en poids d'eau par rapport au poids de la matière première mélangée, 2 à 4 % en poids d'un dispersant par rapport au poids de la matière première mélangée, et 2 à 3 % en poids d'un liant par rapport au poids de la matière première mélangée sont insérés de manière à préparer un mélange à l'état de suspension; une étape de granulation de matière première à base de ferrite (S130) pour sécher par pulvérisation le mélange à l'état de suspension de manière à granuler le mélange; une étape de frittage par traitement thermique (S140) pour chauffer le matériau de ferrite granulaire à une température de 1 000 à 1 400 °C pendant 3 à 8 heures de sorte à fritter un corps fritté en ferrite; et une étape de pulvérisation de corps fritté en ferrite (S150) pour pulvériser le corps fritté en ferrite traité thermiquement en une poudre.
본 발명은 인체에 유익한 기능성 조성물의 제조방법이다. 그 구체적인 공정은 다음과 같다. 산화제2철 45~55중량%, 산화니켈 12~16중량%, 산화아연 14~18중량%, 산화구리 4~6중량%, 리튬 4~8중량%, 바륨 4~8중량% 및 마그네슘 2~4중량%를 혼합하여 페라이트 혼합원료를 조성하는 페라이트 배합공정(S110)과; 상기 혼합원료의 무게에 대하여 물 130~170중량%, 분산제는 혼합원료의 무게에 대하여 2~4중량%, 결착제는 혼합원료의 무게에 대하여 2~3중량%를 투입하여 현탁액 상태의 혼합물로 만드는 페라이트원료의 현탁화 공정(S120)과; 상기 현탁액 상태의 혼합물을 분무 건조하여 과립상으로 만드는 페라이트원료 과립화 공정(S130)과; 과립상의 페라이트원료를 3~8시간 동안 1,000~1,400℃ 온도로 가열하여 페라이트소결체(Ferrite)를 소성하는 열처리 소결공정(S140)과; 상기 열처리된 페라이트소결체를 분말로 분쇄하는 페라이트소결체 분말공정(S150)을 포함하여 이루어진다.
METHOD FOR PRODUCING FUNCTIONAL COMPOSITION BENEFICIAL TO HUMAN BODY
PROCÉDÉ DE PRODUCTION D'UNE COMPOSITION FONCTIONNELLE BÉNÉFIQUE POUR LE CORPS HUMAIN
인체에 유익한 기능성 조성물의 제조방법
IM JUN HWAN (Autor:in)
23.03.2017
Patent
Elektronische Ressource
Koreanisch
IPC:
C04B
Kalk
,
LIME
/
A61L
Verfahren oder Vorrichtungen zum Sterilisieren von Stoffen oder Gegenständen allgemein
,
METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL
/
A61N
ELECTROTHERAPY
,
Elektrotherapie
/
C01G
Verbindungen der von den Unterklassen C01D oder C01F nicht umfassten Metalle
,
COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
/
H05K
PRINTED CIRCUITS
,
Gedruckte Schaltungen
method for producing solid composition and method for producing functional ceramic molded body
| Europäisches Patentamt | 2021
METHOD FOR PRODUCING SOLID COMPOSITION AND METHOD FOR PRODUCING FUNCTIONAL CERAMIC MOLDED BODY
| Europäisches Patentamt | 2021
SOLID COMPOSITION AND METHOD FOR PRODUCING FUNCTIONAL CERAMIC MOLDED BODY
| Europäisches Patentamt | 2021