The present invention relates to a composition based on natural and synthetic waste, for forming ecological roofing for housing (1), developed for the construction industry, more specifically for the production or assembly of roofing structures for houses, buildings and sheds inter alia, characterised in that it consists of three specific components, which are joist, rafter and batten, the formulation of each of said components being the following: the joist consists of 4000 gr. of PVC, 800 gr. of sugarcane bagasse and 01 flat steel bar having a height of 1/8" and a width of 2.5 cm; the rafter consists of 1000 gr. of PVC, 250 gr. of sugarcane bagasse and 01 flat steel bar having a height of 1/8" and a width of 1.0 cm; and the batten consists of 600 gr. of PVC and 160 gr. of sugarcane bagasse. It should be noted that the production or moulding of each of said pieces is performed as follows: the PVC waste is heated until it melts, then the molten PVC is poured into each type of metal mould in order to model the ecological wood, moulds being provided for each one of the pieces, and finally, the product is removed from the mould after 30 minutes, irrespective of the piece.

Le présente brevet d'invention concerne une composition à base de résidus naturels et synthétiques pour la formation d'une couverture écologique pour résidences (1), mise au point en vue d'une application au domaine de la construction civile, notamment pour la fabrication ou le montage de structures de toitures de couvertures de maisons, d'immeubles et de hangars, entre autres, caractérisée en ce qu'elle est constituée par trois éléments spécifiques, soit une barre d'appui, un chevron et une latte, la formulation de chacun de ces éléments étant la suivante : la barre d'appui comprend 4000 g de PVC, 800 g de bagasse de canne à sucre et 01 barre plate d'acier de 1/8'' de hauteur et de 2,5 cm de largeur ; le chevron comprend 1000 g de PVC, 250 g de bagasse de canne à sucre et 01 barre plate d'acier de 1/8'' de hauteur et de 1,0 cm de largeur ; et la latte comprend 600 g de PVC et 160 g de bagasse de canne à sucre. Il convient également de relever que la fabrication ou le moulage de chacune de ces pièces est réalisé de la manière suivante : les résidus de PVC sont chauffés jusqu'à ce qu'ils fondent, puis le PVC fondu est versé dans chaque type de moule métallique en vue du modelage d'un bois écologique, des moules étant en outre utilisés pour chacune des pièces, le produit étant enfin détaché du moule après 30 minutes, indépendamment de la pièce.

A presente patente de Invenção diz respeito a Composição em Base a Resíduos Naturais e Sintéticos para Formação de Cobertura Ecológica Para Residências, (1), a qual foi desenvolvida para atender a área da construção civil, mais especificamente para a fabricação ou montagem de estruturas de telhados de coberturas de casas, prédios e galpões dentre outros, a qual é caracterizada por ser constituída por três componentes específicos, os quais são linha, caibro e ripa, sendo que a formulação de cada um destes componentes é a seguinte : A Linha, é constituída por 4000 gr de PVC; 800 gr de Bagaço de Cana e 01 barra chata de aço com 1/8"de altura e 2,5cm de largura; O Caibro por l000gr de PVC; 250gr de Bagaço de Cana e 01 barra chata de aço com 1/8" de altura e 1,0cm de largura; E a Ripa: 600 gr de PVC e 160 gr de Bagaço de Cana, vale também destacar que a fabricação ou moldagem de cada uma destas peças é realizada da seguinte forma, os resíduos de PVC são esquentados até derreter, a seguir, o PVC derretido é despejado em cada tipo de molde metálico para modelar a madeira ecológica, destacando-se que há moldes para cada uma das peças, e finalmente, independentemente da peça, após 30 minutos desprende-se o produto do molde.