BUILDING WASTE BURN-FREE REGENERATION BRICK AND PREPARATION METHOD THEREOF
The present invention provides a building waste burn-free regeneration brick and a preparation method thereof, with raw materials comprising a gelling material and an aggregate. The aggregate is a regenerated aggregate formed by treatment of building waste, having the characteristics of: a cementing material being used for pumping concrete waste residue, and cement being added to the building waste burn-free regeneration brick raw materials as an activator. The preparation method comprises: (1) weighing the cementing material and the aggregate according to the mixture ratio of the raw materials, reserving for future use; (2) proportionately mixing the gelling material and the aggregate, obtaining a mixture; (3) putting the uniformly stirred mixture into a mold, performing compression molding on the forming machine by utilizing appropriate pressure and loading speed, and immediately removing after forming; (4) performing carbonization maintenance or steam curing on the removed regeneration brick for a certain period of time, obtaining a burn-free regeneration brick. The present invention achieves the goal of waste resource utilization, effectively reduces environmental pollution, reduces manufacturing costs, and has raw materials that are easy to obtain; the preparation method is simple and reasonable, reduces air pollution, and is suitable for large-scale industrial production.
La présente invention concerne une brique de régénération sans combustion de déchets de construction et son procédé de préparation, présentant des matières premières comprenant un matériau gélifiant et un agrégat. L'agrégat est un agrégat régénéré formé par traitement de déchets de construction, présentant les caractéristiques suivantes : un matériau de cimentation est utilisé pour pomper des résidus de déchets de béton, et du ciment est ajouté aux matières premières de brique de régénération sans combustion de déchets de construction en tant qu'activateur. Le procédé de préparation consiste : (1) à peser le matériau de cimentation et l'agrégat en fonction du rapport de mélange des matières premières, à réserver pour une utilisation future ; (2) à mélanger proportionnellement le matériau gélifiant et l'agrégat, à obtenir un mélange ; (3) à placer le mélange uniformément agité dans un moule, à réaliser un moulage par compression sur la machine de formage à l'aide d'une pression appropriée et d'une vitesse de chargement appropriée, et à retirer immédiatement après le formage ; (4) à réaliser un maintien de la carbonisation ou d'un durcissement à la vapeur sur la brique de régénération retirée pendant une certaine période de temps, à obtenir une brique de régénération sans combustion. La présente invention atteint le but d'utilisation de déchets comme ressources, réduit efficacement la pollution de l'environnement, réduit les coûts de fabrication, et a des matières premières qui sont faciles à obtenir ; le procédé de préparation est simple et raisonnable, réduit la pollution de l'air, et est approprié pour une production industrielle à grande échelle.
本发明提供了一种建筑垃圾免烧再生砖及其制备方法，原料包括胶凝材料和骨料，骨料为建筑垃圾处理而成的再生骨料，其特点是：胶凝材料为泵送混凝土废渣，建筑垃圾免烧再生砖的原料中掺加水泥作为激发剂。制备方法包括：(1)按原料配合比称取胶凝材料和骨料，备用；(2)将胶凝材料和骨料按比例混合得到混合料；(3)将搅拌均匀的混合料装入模具，在成型机上采用适当压力与加荷速度压制成型，成型后立即拆模；(4)将拆模后的再生砖进行碳化养护或蒸汽养护一定时间后，得到免烧再生砖。达到废物资源化利用的目的，能够有效地减少环境污染，降低制造成本，且原料易得；制备方法简单、合理，减少空气污染，适用于大规模工业化生产。
BUILDING WASTE BURN-FREE REGENERATION BRICK AND PREPARATION METHOD THEREOF
The present invention provides a building waste burn-free regeneration brick and a preparation method thereof, with raw materials comprising a gelling material and an aggregate. The aggregate is a regenerated aggregate formed by treatment of building waste, having the characteristics of: a cementing material being used for pumping concrete waste residue, and cement being added to the building waste burn-free regeneration brick raw materials as an activator. The preparation method comprises: (1) weighing the cementing material and the aggregate according to the mixture ratio of the raw materials, reserving for future use; (2) proportionately mixing the gelling material and the aggregate, obtaining a mixture; (3) putting the uniformly stirred mixture into a mold, performing compression molding on the forming machine by utilizing appropriate pressure and loading speed, and immediately removing after forming; (4) performing carbonization maintenance or steam curing on the removed regeneration brick for a certain period of time, obtaining a burn-free regeneration brick. The present invention achieves the goal of waste resource utilization, effectively reduces environmental pollution, reduces manufacturing costs, and has raw materials that are easy to obtain; the preparation method is simple and reasonable, reduces air pollution, and is suitable for large-scale industrial production.
La présente invention concerne une brique de régénération sans combustion de déchets de construction et son procédé de préparation, présentant des matières premières comprenant un matériau gélifiant et un agrégat. L'agrégat est un agrégat régénéré formé par traitement de déchets de construction, présentant les caractéristiques suivantes : un matériau de cimentation est utilisé pour pomper des résidus de déchets de béton, et du ciment est ajouté aux matières premières de brique de régénération sans combustion de déchets de construction en tant qu'activateur. Le procédé de préparation consiste : (1) à peser le matériau de cimentation et l'agrégat en fonction du rapport de mélange des matières premières, à réserver pour une utilisation future ; (2) à mélanger proportionnellement le matériau gélifiant et l'agrégat, à obtenir un mélange ; (3) à placer le mélange uniformément agité dans un moule, à réaliser un moulage par compression sur la machine de formage à l'aide d'une pression appropriée et d'une vitesse de chargement appropriée, et à retirer immédiatement après le formage ; (4) à réaliser un maintien de la carbonisation ou d'un durcissement à la vapeur sur la brique de régénération retirée pendant une certaine période de temps, à obtenir une brique de régénération sans combustion. La présente invention atteint le but d'utilisation de déchets comme ressources, réduit efficacement la pollution de l'environnement, réduit les coûts de fabrication, et a des matières premières qui sont faciles à obtenir ; le procédé de préparation est simple et raisonnable, réduit la pollution de l'air, et est approprié pour une production industrielle à grande échelle.
本发明提供了一种建筑垃圾免烧再生砖及其制备方法，原料包括胶凝材料和骨料，骨料为建筑垃圾处理而成的再生骨料，其特点是：胶凝材料为泵送混凝土废渣，建筑垃圾免烧再生砖的原料中掺加水泥作为激发剂。制备方法包括：(1)按原料配合比称取胶凝材料和骨料，备用；(2)将胶凝材料和骨料按比例混合得到混合料；(3)将搅拌均匀的混合料装入模具，在成型机上采用适当压力与加荷速度压制成型，成型后立即拆模；(4)将拆模后的再生砖进行碳化养护或蒸汽养护一定时间后，得到免烧再生砖。达到废物资源化利用的目的，能够有效地减少环境污染，降低制造成本，且原料易得；制备方法简单、合理，减少空气污染，适用于大规模工业化生产。
BUILDING WASTE BURN-FREE REGENERATION BRICK AND PREPARATION METHOD THEREOF
BRIQUE DE RÉGÉNÉRATION SANS COMBUSTION DE DÉCHETS DE CONSTRUCTION ET SON PROCÉDÉ DE PRÉPARATION
一种建筑垃圾免烧再生砖及其制备方法
GAO SONG (Autor:in) / LI SHAOCHUN (Autor:in) / HOU DONGSHUAI (Autor:in) / GONG YAOYAO (Autor:in) / BAN SHUNLI (Autor:in) / JIN ZUQUAN (Autor:in) / ZHANG JIGANG (Autor:in) / LI QIUYI (Autor:in)
31.03.2022
Patent
Elektronische Ressource
Chinesisch
IPC:
C04B
Kalk
,
LIME
/
B28B
Formgeben von Ton oder anderen keramischen Stoffzusammensetzungen, Schlacke oder von Mischungen, die zementartiges Material enthalten, z.B. Putzmörtel
,
SHAPING CLAY OR OTHER CERAMIC COMPOSITIONS, SLAG OR MIXTURES CONTAINING CEMENTITIOUS MATERIAL, e.g. PLASTER
/
B28C
Tonaufbereitung
,
PREPARING CLAY
Building waste shale brick and preparation method thereof
| Europäisches Patentamt | 2015
Building waste regenerated brick and preparation method thereof
| Europäisches Patentamt | 2024
Gangue burn-free brick with antibacterial and antimould effects and preparation method thereof
| Europäisches Patentamt | 2015
Energy-saving burn-free air brick and preparing method thereof
| Europäisches Patentamt | 2016
Thermal-insulation and toughened burn-free colliery wastes brick and preparation method thereof
| Europäisches Patentamt | 2015