Use of Lightweight Concrete for Reducing Cracks in Bridge Decks
Cracks in bridge decks can be due to many factors related to environmental effects, chemical reactions, and structural loads. Careful selection of materials and mixture proportions can minimize cracking to some degree. To reduce cracking, shrinkage must be reduced; however, cracking also depends on other factors such as modulus of elasticity, creep, tensile strength, and restraint. A low modulus of elasticity and high creep help to minimize cracking. Lightweight concrete (LWC) has a lower modulus of elasticity, higher inelastic strains, a lower coefficient of thermal expansion, a more continuous contact zone between the aggregate and the paste, and more water in the pores of aggregates for continued internal curing when compared to normal weight concrete. These properties tend to reduce cracking in the concrete and are highly desirable in bridge decks. The Virginia Department of Transportation (VDOT) has been successfully using LWC in bridge structures. In most of these bridges, the coarse aggregate has been lightweight and the fine aggregate normal weight natural sand. The purpose of this study was to investigate the effectiveness of LWC in reducing cracks in bridge decks. Seven bridges from six VDOT districts were included in the study. Three bridge decks each were constructed in 2012 and 2013, and one was constructed in 2014. The results showed that bridge decks with fewer cracks than were typical of decks constructed with normal weight aggregate over the past 20 years or no cracks can be constructed with LWC mixtures. The study recommends that LWC with a maximum cementitious content of 650 lb/yd3 be used in VDOT bridge deck concrete mixtures.
Use of Lightweight Concrete for Reducing Cracks in Bridge Decks
Cracks in bridge decks can be due to many factors related to environmental effects, chemical reactions, and structural loads. Careful selection of materials and mixture proportions can minimize cracking to some degree. To reduce cracking, shrinkage must be reduced; however, cracking also depends on other factors such as modulus of elasticity, creep, tensile strength, and restraint. A low modulus of elasticity and high creep help to minimize cracking. Lightweight concrete (LWC) has a lower modulus of elasticity, higher inelastic strains, a lower coefficient of thermal expansion, a more continuous contact zone between the aggregate and the paste, and more water in the pores of aggregates for continued internal curing when compared to normal weight concrete. These properties tend to reduce cracking in the concrete and are highly desirable in bridge decks. The Virginia Department of Transportation (VDOT) has been successfully using LWC in bridge structures. In most of these bridges, the coarse aggregate has been lightweight and the fine aggregate normal weight natural sand. The purpose of this study was to investigate the effectiveness of LWC in reducing cracks in bridge decks. Seven bridges from six VDOT districts were included in the study. Three bridge decks each were constructed in 2012 and 2013, and one was constructed in 2014. The results showed that bridge decks with fewer cracks than were typical of decks constructed with normal weight aggregate over the past 20 years or no cracks can be constructed with LWC mixtures. The study recommends that LWC with a maximum cementitious content of 650 lb/yd3 be used in VDOT bridge deck concrete mixtures.
Use of Lightweight Concrete for Reducing Cracks in Bridge Decks
H. Nair (Autor:in) / C. Ozyildirim (Autor:in) / M. M. Sprinkel (Autor:in)
2016
20 pages
Report
Keine Angabe
Englisch
Road Transportation , Transportation & Traffic Planning , Urban Administration & Planning , Transportation , Problem Solving Information for State & Local Governments , Sociopolitical , Transportation Technology , Administration and Planning , Construction Equipment, Materials, & Supplies , Civil Engineering , Construction Management & Techniques , Structural Analyses , Construction Materials, Components, & Equipment , Civil, Construction, Structural, & Building Engineering , Lightweight concrete (LWC) , Bridge deck cracking , Shrinkage cracking , Virginia (State) , Recommenations , Internal curing , Bridge decks , Coarse aggregate , Cementitious , Mixture proportions , Structural analysis (Engineering) , Virginia Department of Transportation (VDOT)
Cracks in concrete bridge decks
| TIBKAT | 1978
Cracks in Concrete Bridge Decks
| NTIS | 1978
Prevention of Cracks in Concrete Bridge Decks
| British Library Conference Proceedings | 1992