Effects of Chemistry and Other Variables on Corrosion and Stress Corrosion Cracking in Hanford Double Shell Tanks
Laboratory testing was performed to develop a comprehensive understanding of the corrosivity of the tank wastes stored in Double-Shell Tanks using simulants primarily from Tanks 241-AP-105, 241-SY-103 and 241-AW-105. Additional tests were conducted using simulants of the waste stored in 241-AZ-102, 241-SY-101, 241-AN-107, and 241-AY-101. This test program placed particular emphasis on defining the range of tank waste chemistries that do not induce the onset of localized forms of corrosion, particularly pitting and stress corrosion cracking. This document summarizes the key findings of the research program.
Effects of Chemistry and Other Variables on Corrosion and Stress Corrosion Cracking in Hanford Double Shell Tanks
Laboratory testing was performed to develop a comprehensive understanding of the corrosivity of the tank wastes stored in Double-Shell Tanks using simulants primarily from Tanks 241-AP-105, 241-SY-103 and 241-AW-105. Additional tests were conducted using simulants of the waste stored in 241-AZ-102, 241-SY-101, 241-AN-107, and 241-AY-101. This test program placed particular emphasis on defining the range of tank waste chemistries that do not induce the onset of localized forms of corrosion, particularly pitting and stress corrosion cracking. This document summarizes the key findings of the research program.
Effects of Chemistry and Other Variables on Corrosion and Stress Corrosion Cracking in Hanford Double Shell Tanks
M. H. Brown (Autor:in)
2008
314 pages
Report
Keine Angabe
Englisch
Radioactive Wastes & Radioactivity , Corrosion & Corrosion Inhibition , Materials Degradation & Fouling , Hanford Reservation , Radioactive waste storage , Stress corrosion , Chemical effects , Tanks , Storage facilities , Pitting corrosion , Crack propagation , Radioactive wastes , Corrosive effects , Laboratory tests
Engineering Index Backfile | 1945
Prevention of Repaired Steel Tanks from Sulfide Corrosion Cracking
| British Library Online Contents | 2004
Effects of testing variables on stress corrosion cracking susceptibility of Al 2024-T351
| British Library Online Contents | 2012
Effects of testing variables on stress corrosion cracking susceptibility of Al 2024-T351
| British Library Online Contents | 2012