Controlled Low-Strength Materials Composed Solely of By-Products
A series of low-cost controlled low-strength materials (CLSM) mixtures were produced without cement, using only by-products, including Class C fly ash, large quantities of limestone quarry fines, and synthetic gypsum. Flow, setting time, compressive strength, elastic modulus, and freezing-and-thawing resistance of mixtures were evaluated. Results indicated that CLSM mixtures solely comprised of by-products can be designed to provide a wide range of flow, setting time, and strength values. Obtained flow values varied between 200 and 600 mm, setting time varied between a couple of hours and a day, and strength values varied between 237.4 and 9932 kPa. The maximum measured mass loss after 12 freezing-and-thawing cycles was 8%. Results showed that, the addition of synthetic gypsum significantly improved strength and freezing-and-thawing resistance of mixtures.
Controlled Low-Strength Materials Composed Solely of By-Products
A series of low-cost controlled low-strength materials (CLSM) mixtures were produced without cement, using only by-products, including Class C fly ash, large quantities of limestone quarry fines, and synthetic gypsum. Flow, setting time, compressive strength, elastic modulus, and freezing-and-thawing resistance of mixtures were evaluated. Results indicated that CLSM mixtures solely comprised of by-products can be designed to provide a wide range of flow, setting time, and strength values. Obtained flow values varied between 200 and 600 mm, setting time varied between a couple of hours and a day, and strength values varied between 237.4 and 9932 kPa. The maximum measured mass loss after 12 freezing-and-thawing cycles was 8%. Results showed that, the addition of synthetic gypsum significantly improved strength and freezing-and-thawing resistance of mixtures.
Controlled Low-Strength Materials Composed Solely of By-Products
Ceki Halmen (Autor:in) / Harsh Shah
ACI materials journal ; 112
2015
Aufsatz (Zeitschrift)
Englisch
| British Library Online Contents | 2016
Evaluation of controlled low strength materials containing industrial by-products
| Online Contents | 2007
Evaluation of controlled low strength materials containing industrial by-products
| British Library Online Contents | 2007
Controlled low strength materials containing industrial by products - A review
| American Institute of Physics | 2024
Controlled Low Strength Materials
British Library Online Contents | 1997