Study of Hydration Process of Cement Paste with Chemical Mapping
In the present study, chemical mapping on the hydration process of cement pastes with water-cement ratios (w/c) of 0.35 to 0.60 was implemented by Raman spectroscopy (RS) from 12 hours after mixing until 28 days. Both the cement ingredients and hydration products were quantitatively studied. From the research, the content of calcium silicates (C^sub 3^S and C^sub 2^S) was observed to decrease rapidly during the first 3 days and then the decreasing rate slowed down. As one of the major hydration products, calcium hydroxide increased and tended to cluster in the pore vicinity with hydration progress. It was the only compound that could be detected as a pure phase in some measured regions. Ettringite was found to form on the surface of the unreacted cement particles, which was shown as a mixed zone of ettringite and calcium silicates in the maps. The RS chemical mapping results concurred with the scanning electron microscopy images collected from the same pastes.
Study of Hydration Process of Cement Paste with Chemical Mapping
In the present study, chemical mapping on the hydration process of cement pastes with water-cement ratios (w/c) of 0.35 to 0.60 was implemented by Raman spectroscopy (RS) from 12 hours after mixing until 28 days. Both the cement ingredients and hydration products were quantitatively studied. From the research, the content of calcium silicates (C^sub 3^S and C^sub 2^S) was observed to decrease rapidly during the first 3 days and then the decreasing rate slowed down. As one of the major hydration products, calcium hydroxide increased and tended to cluster in the pore vicinity with hydration progress. It was the only compound that could be detected as a pure phase in some measured regions. Ettringite was found to form on the surface of the unreacted cement particles, which was shown as a mixed zone of ettringite and calcium silicates in the maps. The RS chemical mapping results concurred with the scanning electron microscopy images collected from the same pastes.
Study of Hydration Process of Cement Paste with Chemical Mapping
Liu, Fengjuan (Autor:in) / Sun, Zhihui
ACI materials journal ; 113
2016
Aufsatz (Zeitschrift)
Englisch
Early Hydration Process of Portland Cement Paste by Electrical Measurement
| British Library Online Contents | 2006
Early Hydration Process of Portland Cement Paste by Electrical Measurement
| Online Contents | 2006
The evolution of cement paste hydration process by impedance spectroscopy
| British Library Online Contents | 2001
Hydration of the cement paste with Na2CO3 addition
| Tema Archiv | 2001
Curing, Hydration, and Microstructure of Cement Paste
| Online Contents | 2006