Micromachining of hardened Portland cement pastes using femtosecond laser pulses
Abstract Femtosecond laser pulses (30 fs in length) of various energies were utilised for production of single and multiple overlapping ablation sites on flat polished surfaces of hardened Portland cement pastes. In order to assess the sizes of the ablation sites and possible subsurface laser-induced damage, the ablation sites were investigated using environmental scanning electron microscopy (ESEM) – both from normal top–down view and in cross-sections. Furthermore, approximately 10-µm wide notches were produced using femtosecond pulses on cylindrical microspecimens (150 µm in diameter) of hardened Portland cement pastes. In addition to electron microscopy observations, several microspecimens were investigated using synchrotron-based X-ray computed microtomography (SRμCT). The results suggest that production of “damage-free” samples for micromechanical testing of hardened Portland cements pastes is possible.
Micromachining of hardened Portland cement pastes using femtosecond laser pulses
Abstract Femtosecond laser pulses (30 fs in length) of various energies were utilised for production of single and multiple overlapping ablation sites on flat polished surfaces of hardened Portland cement pastes. In order to assess the sizes of the ablation sites and possible subsurface laser-induced damage, the ablation sites were investigated using environmental scanning electron microscopy (ESEM) – both from normal top–down view and in cross-sections. Furthermore, approximately 10-µm wide notches were produced using femtosecond pulses on cylindrical microspecimens (150 µm in diameter) of hardened Portland cement pastes. In addition to electron microscopy observations, several microspecimens were investigated using synchrotron-based X-ray computed microtomography (SRμCT). The results suggest that production of “damage-free” samples for micromechanical testing of hardened Portland cements pastes is possible.
Micromachining of hardened Portland cement pastes using femtosecond laser pulses
Trtik, P. (Autor:in) / Hauri, C. P. (Autor:in)
2006
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Micromachining of hardened Portland cement pastes using femtosecond laser pulses
| Online Contents | 2006
Micromachining of hardened Portland cement pastes using femtosecond laser pulses
| Online Contents | 2007
Micromachining of hardened Portland cement pastes using femtosecond laser pulses
| Springer Verlag | 2007
Micromachining of hardened Portland cement pastes using femtosecond laser pulses
| British Library Online Contents | 2007
Porosity of hardened Portland cement pastes
| Engineering Index Backfile | 1956