Initiation of localized steel corrosion in alkaline sulfate solution
https://orcid.org/0000-0003-0726-7667
Abstract The role of sulfate ions on corrosion of steel in alkaline solutions (including cementitious materials) has been contested in the literature due to the effects of the many exposures, material and test conditions. Recent observations of steel corrosion in cementitious grouts in post-tensioned bridges coinciding with elevated sulfate-ion concentrations have prompted the development of material specifications concerning segregated grout. Electrochemical testing of steel in alkaline sulfate solutions were conducted to elucidate the impairment of the passive layer. The increase in the anodic current exchange density at higher sulfate ion concentrations resulted in the development of electronegative potentials and high corrosion rates. The numerous distinct electrochemical noise events in solutions with > 1,300 ppm $ SO_{4} $2− were characteristic of metastable pitting and pitting. The results of the testing identified sulfate levels that impair the passive layer and provided support for recent specifications that limited sulfate ion concentrations in deficient grout.
Initiation of localized steel corrosion in alkaline sulfate solution
https://orcid.org/0000-0003-0726-7667
Abstract The role of sulfate ions on corrosion of steel in alkaline solutions (including cementitious materials) has been contested in the literature due to the effects of the many exposures, material and test conditions. Recent observations of steel corrosion in cementitious grouts in post-tensioned bridges coinciding with elevated sulfate-ion concentrations have prompted the development of material specifications concerning segregated grout. Electrochemical testing of steel in alkaline sulfate solutions were conducted to elucidate the impairment of the passive layer. The increase in the anodic current exchange density at higher sulfate ion concentrations resulted in the development of electronegative potentials and high corrosion rates. The numerous distinct electrochemical noise events in solutions with > 1,300 ppm $ SO_{4} $2− were characteristic of metastable pitting and pitting. The results of the testing identified sulfate levels that impair the passive layer and provided support for recent specifications that limited sulfate ion concentrations in deficient grout.
Initiation of localized steel corrosion in alkaline sulfate solution
https://orcid.org/0000-0003-0726-7667
Abstract The role of sulfate ions on corrosion of steel in alkaline solutions (including cementitious materials) has been contested in the literature due to the effects of the many exposures, material and test conditions. Recent observations of steel corrosion in cementitious grouts in post-tensioned bridges coinciding with elevated sulfate-ion concentrations have prompted the development of material specifications concerning segregated grout. Electrochemical testing of steel in alkaline sulfate solutions were conducted to elucidate the impairment of the passive layer. The increase in the anodic current exchange density at higher sulfate ion concentrations resulted in the development of electronegative potentials and high corrosion rates. The numerous distinct electrochemical noise events in solutions with > 1,300 ppm $ SO_{4} $2− were characteristic of metastable pitting and pitting. The results of the testing identified sulfate levels that impair the passive layer and provided support for recent specifications that limited sulfate ion concentrations in deficient grout.
Initiation of localized steel corrosion in alkaline sulfate solution
Permeh, Samanbar (Autor:in) / Lau, Kingsley (Autor:in) / Duncan, Matthew (Autor:in) / Simmons, Ron (Autor:in)
2021
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Initiation of localized steel corrosion in alkaline sulfate solution
| Springer Verlag | 2021
Localized Corrosion Initiation on Magnesium Alloys
| British Library Online Contents | 1992
| British Library Online Contents | 2000
Localized alkaline corrosion of alloy AA5083 in neutral 3.5% NaCl solution
| British Library Online Contents | 2001