Fire retardancy of a new polypropylene-grafted starch
Reaction to fire of several intumescent Gaialene formulations (Gaialene is a polypropylene-grafted starch) was investigated by mass loss cone calorimeter. Formulations exhibiting promising results were optimized by a design of experiments using mass loss cone calorimeter, UL-94, and limiting oxygen index tests as response. It is shown that melamine-/ammonium polyphosphate–based formulations do not exhibit as good results as ammonium polyphosphate used alone. High performance is observed for 30 wt% ammonium polyphosphate: 60% reduction of the peak heat release rate, high limiting oxygen index (30 vol% O2), and UL-94 V0 ranking at 1.6 mm (V2 at 0.8 mm).
Fire retardancy of a new polypropylene-grafted starch
Reaction to fire of several intumescent Gaialene formulations (Gaialene is a polypropylene-grafted starch) was investigated by mass loss cone calorimeter. Formulations exhibiting promising results were optimized by a design of experiments using mass loss cone calorimeter, UL-94, and limiting oxygen index tests as response. It is shown that melamine-/ammonium polyphosphate–based formulations do not exhibit as good results as ammonium polyphosphate used alone. High performance is observed for 30 wt% ammonium polyphosphate: 60% reduction of the peak heat release rate, high limiting oxygen index (30 vol% O2), and UL-94 V0 ranking at 1.6 mm (V2 at 0.8 mm).
Fire retardancy of a new polypropylene-grafted starch
Dupretz, Renaud (Autor:in) / Fontaine, Gaëlle (Autor:in) / Bourbigot, Serge (Autor:in)
Journal of Fire Sciences ; 31 ; 563-575
01.11.2013
13 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Fire retardancy of a new polypropylene-grafted starch
| Online Contents | 2013
Fire retardancy of a new polypropylene-grafted starch: Part II: investigation of mechanisms
| SAGE Publications | 2014
Fire retardancy of a new polypropylene-grafted starch: Part II: investigation of mechanisms
| Online Contents | 2014
Fire Retardancy of Polypropylene-Metal Hydroxide Nanocomposites
| British Library Conference Proceedings | 2006
Fire retardancy of polypropylene composites using intumescent coatings
| Tema Archiv | 2008