Preparation and characterization of early strength polycarboxylate superplasticizer
Through the adjustment of polyether monomer, polyether molecular weight and early strength functional monomer, the best process formula was determined, and its molecular weight was tested by gel permeation chromatography, as well as the product performance. The experimental results showed that the early strength polycarboxylate water reducer (ES-PCE)was prepared by solution polymerization using a vinyl polyoxyethylene ether with a molecular weight of 5000 and a 2-acrylamido-methylpropane sulfonic acid in the ammonium persulfate, hydrogen peroxide, and sodium bisulfite initiator system. Compared with similar products PC-1 and PC-2, the compressive strength of ES-PCE at 1d, 7d, and 28d was comparable to that of similar products PC-1, Compared to similar domestic products PC-2, it is about 2 ~ 3 MPa higher, indicating that ES-PCE can completely replace similar foreign products, to improve template turnover rate. Thereby it promotes the rapid development of prefabricated buildings.
Preparation and characterization of early strength polycarboxylate superplasticizer
Through the adjustment of polyether monomer, polyether molecular weight and early strength functional monomer, the best process formula was determined, and its molecular weight was tested by gel permeation chromatography, as well as the product performance. The experimental results showed that the early strength polycarboxylate water reducer (ES-PCE)was prepared by solution polymerization using a vinyl polyoxyethylene ether with a molecular weight of 5000 and a 2-acrylamido-methylpropane sulfonic acid in the ammonium persulfate, hydrogen peroxide, and sodium bisulfite initiator system. Compared with similar products PC-1 and PC-2, the compressive strength of ES-PCE at 1d, 7d, and 28d was comparable to that of similar products PC-1, Compared to similar domestic products PC-2, it is about 2 ~ 3 MPa higher, indicating that ES-PCE can completely replace similar foreign products, to improve template turnover rate. Thereby it promotes the rapid development of prefabricated buildings.
Preparation and characterization of early strength polycarboxylate superplasticizer
Advances in Engineering res
Li, Dayong (Herausgeber:in) / Zhang, Yu (Herausgeber:in) / Luan, Yalin (Herausgeber:in) / Ke, Yuliang (Autor:in) / Fang, Yunhui (Autor:in) / Ma, Xiuxing (Autor:in) / Guo, Yuanqiang (Autor:in) / Zhong, Lina (Autor:in) / Chen, Hao (Autor:in)
International Conference on Architectural, Civil and Hydraulic Engineering ; 2023 ; Qingdao, China
28.12.2023
8 pages
Aufsatz/Kapitel (Buch)
Elektronische Ressource
Englisch
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2016
| Europäisches Patentamt | 2016
Novel early-strength polycarboxylate superplasticizer
| Europäisches Patentamt | 2021
Preparation method of early-strength polycarboxylate superplasticizer
| Europäisches Patentamt | 2020