Fatigue damage development in 10CrMo9-10 steel for power plant pipes in as-received state and after 280,000 h of exploitation
https://orcid.org/http://orcid.org/0000-0001-9565-3407
This paper discusses an effect of 280,000 h of exploitation under internal pressure of 2.9 MPa and high temperature of 540 °C on the mechanical properties of 10CrMo9-10 (10H2M) power engineering steel. The mechanical response of the specimens obtained from two pipes: a new in the as-received state and exploited for a long period was assessed through the uniaxial tensile tests and subsequent fatigue tests. The long-term, high-temperature exposure of 10H2M steel resulted in the deterioration of its mechanical properties and was quantitatively described as a function of the fatigue damage measure, φ, and the fatigue damage parameter D. Finally, the proposed methodology of power exponent approximation with both damage sensitive parameters (φ, D) enabled for successful determination of the 10H2M steel fatigue life.
Fatigue damage development in 10CrMo9-10 steel for power plant pipes in as-received state and after 280,000 h of exploitation
https://orcid.org/http://orcid.org/0000-0001-9565-3407
This paper discusses an effect of 280,000 h of exploitation under internal pressure of 2.9 MPa and high temperature of 540 °C on the mechanical properties of 10CrMo9-10 (10H2M) power engineering steel. The mechanical response of the specimens obtained from two pipes: a new in the as-received state and exploited for a long period was assessed through the uniaxial tensile tests and subsequent fatigue tests. The long-term, high-temperature exposure of 10H2M steel resulted in the deterioration of its mechanical properties and was quantitatively described as a function of the fatigue damage measure, φ, and the fatigue damage parameter D. Finally, the proposed methodology of power exponent approximation with both damage sensitive parameters (φ, D) enabled for successful determination of the 10H2M steel fatigue life.
Fatigue damage development in 10CrMo9-10 steel for power plant pipes in as-received state and after 280,000 h of exploitation
https://orcid.org/http://orcid.org/0000-0001-9565-3407
This paper discusses an effect of 280,000 h of exploitation under internal pressure of 2.9 MPa and high temperature of 540 °C on the mechanical properties of 10CrMo9-10 (10H2M) power engineering steel. The mechanical response of the specimens obtained from two pipes: a new in the as-received state and exploited for a long period was assessed through the uniaxial tensile tests and subsequent fatigue tests. The long-term, high-temperature exposure of 10H2M steel resulted in the deterioration of its mechanical properties and was quantitatively described as a function of the fatigue damage measure, φ, and the fatigue damage parameter D. Finally, the proposed methodology of power exponent approximation with both damage sensitive parameters (φ, D) enabled for successful determination of the 10H2M steel fatigue life.
Fatigue damage development in 10CrMo9-10 steel for power plant pipes in as-received state and after 280,000 h of exploitation
Archiv.Civ.Mech.Eng
Kopec, Mateusz (Autor:in) / Brodecki, Adam (Autor:in) / Kowalewski, Zbigniew L. (Autor:in)
23.03.2023
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| Springer Verlag | 2023
Failure analysis of a 12Cr1MoV superheater tube after 280,000 h of service
| DOAJ | 2024
Engineering Index Backfile | 1938
| British Library Online Contents | 2015
X-ray diffraction study of microstructural changes during fatigue damage initiation in steel pipes
| British Library Online Contents | 2012