Crack growth resistance in fibre reinforced alkali-activated fly ash concrete exposed to extreme temperatures
Abstract This paper examines the crack growth resistance of alkali-activated fly ash concrete under extreme temperatures. Plain and hybrid fibre reinforced alkali activated concrete prepared with fly ash were subjected to a range of temperatures from − 30 to 300 °C, sustained for 2 h. The alkali activation was effected with a blend of sodium hydroxide and sodium silicate. A fibre blend of steel to polypropylene in the volume ratio of 4:1 and a total as high as 1% by volume fraction reinforced the mixtures. The resulting systems were examined for residual strength under compression and splitting tension. Further, notched prisms were loaded under 4-point flexure to evaluate the residual fracture toughness. Based on the results, four different stages for fracture behaviour were identified with superior fibre efficiency seen at sub-zero temperatures. Across the breadth of temperatures examined, adding fibres led to higher residual fracture toughness for those systems that displayed a narrow range of thermal conductivity.
Crack growth resistance in fibre reinforced alkali-activated fly ash concrete exposed to extreme temperatures
Abstract This paper examines the crack growth resistance of alkali-activated fly ash concrete under extreme temperatures. Plain and hybrid fibre reinforced alkali activated concrete prepared with fly ash were subjected to a range of temperatures from − 30 to 300 °C, sustained for 2 h. The alkali activation was effected with a blend of sodium hydroxide and sodium silicate. A fibre blend of steel to polypropylene in the volume ratio of 4:1 and a total as high as 1% by volume fraction reinforced the mixtures. The resulting systems were examined for residual strength under compression and splitting tension. Further, notched prisms were loaded under 4-point flexure to evaluate the residual fracture toughness. Based on the results, four different stages for fracture behaviour were identified with superior fibre efficiency seen at sub-zero temperatures. Across the breadth of temperatures examined, adding fibres led to higher residual fracture toughness for those systems that displayed a narrow range of thermal conductivity.
Crack growth resistance in fibre reinforced alkali-activated fly ash concrete exposed to extreme temperatures
Goncalves, Jose R. A. (Autor:in) / Boluk, Yaman (Autor:in) / Bindiganavile, Vivek (Autor:in)
Materials and Structures ; 51 ; 1-10
26.02.2018
10 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Alkali-activated binders , Fibre reinforced systems , Fracture and crack-growth resistance , Geopolymer , Thermal effects , Toughness Engineering , Structural Mechanics , Materials Science, general , Theoretical and Applied Mechanics , Operating Procedures, Materials Treatment , Civil Engineering , Building Materials
| British Library Conference Proceedings | 2016
| British Library Online Contents | 2016