Modification of Wood-Polymer Composites with Silica Sols of Different Nature
https://orcid.org/http://orcid.org/0000-0002-3039-5408
https://orcid.org/http://orcid.org/0000-0003-3905-5730
https://orcid.org/http://orcid.org/0000-0003-0874-316X
https://orcid.org/http://orcid.org/0000-0002-3448-7369
At the present time the actual task in the development of compositions for profile molding products made of wood-polymer composites is the search for effective binding agents for the system wood filler - polymer. In this work, we investigated the influence of different types of silica as binding agents on the properties of wood-polymer composites based on polyvinyl chloride. Silica sols had different stabilizing media, pH values and silica content. Tests were carried out on film samples obtained by rolling. Both technological and operational properties of the studied composites were considered. It was found that the introduction of silica, regardless of their type, increases the tensile strength. At the same time composites modified with silica with higher SiO2 content (about 30%), have increased values of strength characteristics. It was also found that silica sols stabilized with sodium ions (Na+) do not lead to an increase in melt viscosity.
Modification of Wood-Polymer Composites with Silica Sols of Different Nature
https://orcid.org/http://orcid.org/0000-0002-3039-5408
https://orcid.org/http://orcid.org/0000-0003-3905-5730
https://orcid.org/http://orcid.org/0000-0003-0874-316X
https://orcid.org/http://orcid.org/0000-0002-3448-7369
At the present time the actual task in the development of compositions for profile molding products made of wood-polymer composites is the search for effective binding agents for the system wood filler - polymer. In this work, we investigated the influence of different types of silica as binding agents on the properties of wood-polymer composites based on polyvinyl chloride. Silica sols had different stabilizing media, pH values and silica content. Tests were carried out on film samples obtained by rolling. Both technological and operational properties of the studied composites were considered. It was found that the introduction of silica, regardless of their type, increases the tensile strength. At the same time composites modified with silica with higher SiO2 content (about 30%), have increased values of strength characteristics. It was also found that silica sols stabilized with sodium ions (Na+) do not lead to an increase in melt viscosity.
Modification of Wood-Polymer Composites with Silica Sols of Different Nature
https://orcid.org/http://orcid.org/0000-0002-3039-5408
https://orcid.org/http://orcid.org/0000-0003-3905-5730
https://orcid.org/http://orcid.org/0000-0003-0874-316X
https://orcid.org/http://orcid.org/0000-0002-3448-7369
At the present time the actual task in the development of compositions for profile molding products made of wood-polymer composites is the search for effective binding agents for the system wood filler - polymer. In this work, we investigated the influence of different types of silica as binding agents on the properties of wood-polymer composites based on polyvinyl chloride. Silica sols had different stabilizing media, pH values and silica content. Tests were carried out on film samples obtained by rolling. Both technological and operational properties of the studied composites were considered. It was found that the introduction of silica, regardless of their type, increases the tensile strength. At the same time composites modified with silica with higher SiO2 content (about 30%), have increased values of strength characteristics. It was also found that silica sols stabilized with sodium ions (Na+) do not lead to an increase in melt viscosity.
Modification of Wood-Polymer Composites with Silica Sols of Different Nature
Lecture Notes in Civil Engineering
Vatin, Nikolai (Herausgeber:in) / Khantimirov, Ayaz (Autor:in) / Abdrakhmanova, Lyaylya (Autor:in) / Khozin, Vadim (Autor:in) / Nizamov, Rashit (Autor:in)
International Scientific Conference on Socio-Technical Construction and Civil Engineering ; 2022 ; Kazan, Russia
30.09.2022
8 pages
Aufsatz/Kapitel (Buch)
Elektronische Ressource
Englisch
Characteristics of Activated Silica Sols
| Wiley | 1949
Modification of Wood Flour with Maleic Anhydride for Manufacture of Wood-Polymer Composites
| British Library Online Contents | 2006
New Method of Preparing Activated Silica Sols
| Wiley | 1958
Dispersion of kaolin powders in silica sols
| Online Contents | 2010