Effect of polypropylene fibre reinforced mortars on steel reinforcement corrosion induced by carbonation
Abstract Low amounts of polypropylene fibres are added to concrete as a secondary reinforcement to control cracking. Whether this addition might improve the corrosion resistance of the concrete reinforcement by increasing the resistance to carbonation, via reducing penetrating paths, is the subject addressed in the present paper. Crack control by the fibres in plastic state mortars and crack evolution with time have been studied. Furthermore, the influence of crack width on the steel bar corrosion induced by carbonation has also been monitored. Circular specimens made of mortar have been employed in the experimental phase of the study, using a water/cement ratio of 0.50 and cement/sand ratio of 2/1. The polypropylene fibre content was 0% and 0.5% by volume. Low modulus polypropylene fibres may control the crack width in specimens subjected to inadequate curing conditions. No relationship between crack width and time for corrosion initiation has been observed. However, a beneficial effect of fibre addition on the corrosion rate was found.
Résumé De petites quantités de fibres de polypropylène sont ajoutées au béton comme renforcement secondaire pour éviter la fissuration. L’objet de cet article est de déterminer si l’ajout des fibres peut améliorer la résistance à la corrosion de l’armature métallique par la réduction des chemins de propagation. La réduction de la fissuration par l’ajout de fibres dans des mortiers frais et l’évolution de la fissuration dans le temps ont été étudiées. De plus, on a mesuré l’influence de la largueur des fissures sur la corrosion des armatures métalliques provoquée par la carbonatation. Les éprouvettes étaient des disques de mortier ayant un rapport eau/ciment de 0,50 et un rapport ciment/sable de 2/1. La teneur en fibres de polypropylène était de 0% et 0,5% en volume. Des fibres de module faible peuvent contrôler l’épaisseur des fissures dans des éprouvettes soumises à une mauvaise cure. Aucune relation entre l’épaisseur de la fissure et le temps pour l’initiation de la corrosion n’a été constatée. Cependant, on a trouvé que l’ajout de fibres a un effet bénéfique sur le taux de corrosion.
Effect of polypropylene fibre reinforced mortars on steel reinforcement corrosion induced by carbonation
Abstract Low amounts of polypropylene fibres are added to concrete as a secondary reinforcement to control cracking. Whether this addition might improve the corrosion resistance of the concrete reinforcement by increasing the resistance to carbonation, via reducing penetrating paths, is the subject addressed in the present paper. Crack control by the fibres in plastic state mortars and crack evolution with time have been studied. Furthermore, the influence of crack width on the steel bar corrosion induced by carbonation has also been monitored. Circular specimens made of mortar have been employed in the experimental phase of the study, using a water/cement ratio of 0.50 and cement/sand ratio of 2/1. The polypropylene fibre content was 0% and 0.5% by volume. Low modulus polypropylene fibres may control the crack width in specimens subjected to inadequate curing conditions. No relationship between crack width and time for corrosion initiation has been observed. However, a beneficial effect of fibre addition on the corrosion rate was found.
Résumé De petites quantités de fibres de polypropylène sont ajoutées au béton comme renforcement secondaire pour éviter la fissuration. L’objet de cet article est de déterminer si l’ajout des fibres peut améliorer la résistance à la corrosion de l’armature métallique par la réduction des chemins de propagation. La réduction de la fissuration par l’ajout de fibres dans des mortiers frais et l’évolution de la fissuration dans le temps ont été étudiées. De plus, on a mesuré l’influence de la largueur des fissures sur la corrosion des armatures métalliques provoquée par la carbonatation. Les éprouvettes étaient des disques de mortier ayant un rapport eau/ciment de 0,50 et un rapport ciment/sable de 2/1. La teneur en fibres de polypropylène était de 0% et 0,5% en volume. Des fibres de module faible peuvent contrôler l’épaisseur des fissures dans des éprouvettes soumises à une mauvaise cure. Aucune relation entre l’épaisseur de la fissure et le temps pour l’initiation de la corrosion n’a été constatée. Cependant, on a trouvé que l’ajout de fibres a un effet bénéfique sur le taux de corrosion.
Effect of polypropylene fibre reinforced mortars on steel reinforcement corrosion induced by carbonation
Sanjuán, M. A. (Autor:in) / Andrade, C. (Autor:in) / Bentur, A. (Autor:in)
Materials and Structures ; 31 ; 343-349
01.06.1998
7 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| British Library Online Contents | 1998
Carbonation induced corrosion of reinforcement
| British Library Conference Proceedings | 2002
Fibre Reinforced Cement Mortars
| British Library Conference Proceedings | 1997