Steam-Assisted Synthesis of Hierarchical Fe-Silicalite-1: A Novel Heterogeneous Fenton Catalyst
https://orcid.org/https://orcid.org/0000-0001-9256-0475
https://orcid.org/https://orcid.org/0000-0001-6612-678X
https://orcid.org/https://orcid.org/0000-0002-3897-0817
https://orcid.org/https://orcid.org/0000-0003-3998-7204
https://orcid.org/https://orcid.org/0000-0003-2200-884X
Three types of heterogeneous Fenton catalysts based on Fe-silicalite-1 were synthesized: (1) microcrystals with an average size of 5 μm (m-FeZ); (2) a hierarchical porous sample consisting of 100–200 nm nanocrystals prepared using a dry polystyrene latex template (h-FeZ); and (3) three hierarchical porous samples consisting of 30–50 nm nanocrystals prepared by steam-assisted crystallization (n-FeZ-1,2,3). The synthesis procedure for n-FeZ-1 and n-FeZ-2 included gel pretreatment at 90°C for 72 h. This pretreatment specifically involved introducing Fe into the reaction mixture after (for n-FeZ-1) and before (for n-FeZ-2) the gel aging. The samples were tested as heterogeneous Fenton catalysts in H2O2-mediated total oxidation of ethanol. The performance of the heterogeneous catalysts was compared with a conventional homogeneous Fenton catalyst.
Steam-Assisted Synthesis of Hierarchical Fe-Silicalite-1: A Novel Heterogeneous Fenton Catalyst
https://orcid.org/https://orcid.org/0000-0001-9256-0475
https://orcid.org/https://orcid.org/0000-0001-6612-678X
https://orcid.org/https://orcid.org/0000-0002-3897-0817
https://orcid.org/https://orcid.org/0000-0003-3998-7204
https://orcid.org/https://orcid.org/0000-0003-2200-884X
Three types of heterogeneous Fenton catalysts based on Fe-silicalite-1 were synthesized: (1) microcrystals with an average size of 5 μm (m-FeZ); (2) a hierarchical porous sample consisting of 100–200 nm nanocrystals prepared using a dry polystyrene latex template (h-FeZ); and (3) three hierarchical porous samples consisting of 30–50 nm nanocrystals prepared by steam-assisted crystallization (n-FeZ-1,2,3). The synthesis procedure for n-FeZ-1 and n-FeZ-2 included gel pretreatment at 90°C for 72 h. This pretreatment specifically involved introducing Fe into the reaction mixture after (for n-FeZ-1) and before (for n-FeZ-2) the gel aging. The samples were tested as heterogeneous Fenton catalysts in H2O2-mediated total oxidation of ethanol. The performance of the heterogeneous catalysts was compared with a conventional homogeneous Fenton catalyst.
Steam-Assisted Synthesis of Hierarchical Fe-Silicalite-1: A Novel Heterogeneous Fenton Catalyst
https://orcid.org/https://orcid.org/0000-0001-9256-0475
https://orcid.org/https://orcid.org/0000-0001-6612-678X
https://orcid.org/https://orcid.org/0000-0002-3897-0817
https://orcid.org/https://orcid.org/0000-0003-3998-7204
https://orcid.org/https://orcid.org/0000-0003-2200-884X
Three types of heterogeneous Fenton catalysts based on Fe-silicalite-1 were synthesized: (1) microcrystals with an average size of 5 μm (m-FeZ); (2) a hierarchical porous sample consisting of 100–200 nm nanocrystals prepared using a dry polystyrene latex template (h-FeZ); and (3) three hierarchical porous samples consisting of 30–50 nm nanocrystals prepared by steam-assisted crystallization (n-FeZ-1,2,3). The synthesis procedure for n-FeZ-1 and n-FeZ-2 included gel pretreatment at 90°C for 72 h. This pretreatment specifically involved introducing Fe into the reaction mixture after (for n-FeZ-1) and before (for n-FeZ-2) the gel aging. The samples were tested as heterogeneous Fenton catalysts in H2O2-mediated total oxidation of ethanol. The performance of the heterogeneous catalysts was compared with a conventional homogeneous Fenton catalyst.
Steam-Assisted Synthesis of Hierarchical Fe-Silicalite-1: A Novel Heterogeneous Fenton Catalyst
Pet. Chem.
Bragina, A. A. (Autor:in) / Babina, K. A. (Autor:in) / Kuleshov, D. V. (Autor:in) / Lysikov, A. I. (Autor:in) / Parkhomchuk, E. V. (Autor:in)
Petroleum Chemistry ; 63 ; 158-166
01.02.2023
9 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Cu-modified alkalinized g-C3N4 as photocatalytically assisted heterogeneous Fenton-like catalyst
| British Library Online Contents | 2017
| British Library Online Contents | 2008
Hydrothermal synthesis of hierarchical titanium silicalite-1 using single template
| British Library Online Contents | 2011
Hierarchical silicalite-1 structures based on pyrolized materials
| British Library Online Contents | 2011
Preparation method of green and efficient heterogeneous Fenton catalyst
| Europäisches Patentamt | 2024