Prediction of moisture diffusion and failure in glass/steel adhesive joints
https://orcid.org/http://orcid.org/0000-0001-9614-0515
https://orcid.org/http://orcid.org/0000-0003-2442-3326
Glass/steel adhesive joints are being used increasingly in the construction industry as they offer significant structural advantages over conventional mechanical fastener approaches. However, adhesive joints are also known to be sensitive to moisture diffusion into the bondline, which reduces the interfacial bonding strength for hybrid glass/steel substrates. The effect of moisture on the performance degradation of glass/steel adhesive joints has been successfully predicted assuming adhesive property degradation but requires experimental determination of the affected moisture ingress zone. This study utilizes a multi-physics numerical approach implemented via the commercial finite element code Abaqus 2020, which firstly simulates moisture ingress into the adhesive/glass interface and subsequently couples the diffusion effects with a cohesive zone modelling approach for damage initiation and propagation. The numerical predictions are calibrated against experimental data on glass/steel Double Cantilever Beam (DCB) specimens, which are bonded with a ductile methacrylate adhesive (Araldite 2047–1). The modelling approach is then validated against the experimental response of large double lap shear joints of a significantly different bondline geometry. It is demonstrated that the numerical model successfully predicts the critical exposure time for partial to complete joint degradation enabling the development of engineering guidelines for life-time prediction of various joint geometries.
Prediction of moisture diffusion and failure in glass/steel adhesive joints
https://orcid.org/http://orcid.org/0000-0001-9614-0515
https://orcid.org/http://orcid.org/0000-0003-2442-3326
Glass/steel adhesive joints are being used increasingly in the construction industry as they offer significant structural advantages over conventional mechanical fastener approaches. However, adhesive joints are also known to be sensitive to moisture diffusion into the bondline, which reduces the interfacial bonding strength for hybrid glass/steel substrates. The effect of moisture on the performance degradation of glass/steel adhesive joints has been successfully predicted assuming adhesive property degradation but requires experimental determination of the affected moisture ingress zone. This study utilizes a multi-physics numerical approach implemented via the commercial finite element code Abaqus 2020, which firstly simulates moisture ingress into the adhesive/glass interface and subsequently couples the diffusion effects with a cohesive zone modelling approach for damage initiation and propagation. The numerical predictions are calibrated against experimental data on glass/steel Double Cantilever Beam (DCB) specimens, which are bonded with a ductile methacrylate adhesive (Araldite 2047–1). The modelling approach is then validated against the experimental response of large double lap shear joints of a significantly different bondline geometry. It is demonstrated that the numerical model successfully predicts the critical exposure time for partial to complete joint degradation enabling the development of engineering guidelines for life-time prediction of various joint geometries.
Prediction of moisture diffusion and failure in glass/steel adhesive joints
https://orcid.org/http://orcid.org/0000-0001-9614-0515
https://orcid.org/http://orcid.org/0000-0003-2442-3326
Glass/steel adhesive joints are being used increasingly in the construction industry as they offer significant structural advantages over conventional mechanical fastener approaches. However, adhesive joints are also known to be sensitive to moisture diffusion into the bondline, which reduces the interfacial bonding strength for hybrid glass/steel substrates. The effect of moisture on the performance degradation of glass/steel adhesive joints has been successfully predicted assuming adhesive property degradation but requires experimental determination of the affected moisture ingress zone. This study utilizes a multi-physics numerical approach implemented via the commercial finite element code Abaqus 2020, which firstly simulates moisture ingress into the adhesive/glass interface and subsequently couples the diffusion effects with a cohesive zone modelling approach for damage initiation and propagation. The numerical predictions are calibrated against experimental data on glass/steel Double Cantilever Beam (DCB) specimens, which are bonded with a ductile methacrylate adhesive (Araldite 2047–1). The modelling approach is then validated against the experimental response of large double lap shear joints of a significantly different bondline geometry. It is demonstrated that the numerical model successfully predicts the critical exposure time for partial to complete joint degradation enabling the development of engineering guidelines for life-time prediction of various joint geometries.
Prediction of moisture diffusion and failure in glass/steel adhesive joints
Glass Struct Eng
Katsivalis, Ioannis (Autor:in) / Feih, Stefanie (Autor:in)
Glass Structures & Engineering ; 7 ; 381-397
01.10.2022
17 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Strength evaluation and failure prediction of bolted and adhesive glass/steel joints
| Springer Verlag | 2018
Strength evaluation and failure prediction of bolted and adhesive glass/steel joints
| Online Contents | 2018
Multi-physics Modelling of Moisture Diffusion in the FRP-Concrete Adhesive Joints
| Springer Verlag | 2023
Moisture Absorption Effect on Adhesive Filled Bonded Joints
| British Library Online Contents | 1998
| British Library Online Contents | 2011