Fatigue Design Criteria for Adhesively Bonded Anchorage for CFRP Tendon

Xie, Gui-Hua / Wang, C. M. / Xie, Fu-Zhe / Bian, Yu-Long

Abstract The fatigue failure criterion for the adhesively bonded anchorage system for CFRP (Carbon Fibre Reinforced Polymer) tendon has been investigated in this study. A closed-form shear stress solution was deduced for the static performance of the anchorage system, based on which the fatigue failure criterion was discussed and an analytical model was presented to judge the safety of the anchorage system under fatigue loading by using CLD (Constant Life Diagram) method. The results show that the Smith criterion is suitable for the analysis of fatigue failure occurred in the adhesively bonded anchorage system while the Goodman criterion may lead to risk. The stress concentration caused by manufacturing defects in the adhesively bonded anchorage system influences the occurrence of the fatigue failure and should be considered into the fatigue failure.

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Fatigue Design Criteria for Adhesively Bonded Anchorage for CFRP Tendon

Xie, Gui-Hua / Wang, C. M. / Xie, Fu-Zhe / Bian, Yu-Long

Abstract The fatigue failure criterion for the adhesively bonded anchorage system for CFRP (Carbon Fibre Reinforced Polymer) tendon has been investigated in this study. A closed-form shear stress solution was deduced for the static performance of the anchorage system, based on which the fatigue failure criterion was discussed and an analytical model was presented to judge the safety of the anchorage system under fatigue loading by using CLD (Constant Life Diagram) method. The results show that the Smith criterion is suitable for the analysis of fatigue failure occurred in the adhesively bonded anchorage system while the Goodman criterion may lead to risk. The stress concentration caused by manufacturing defects in the adhesively bonded anchorage system influences the occurrence of the fatigue failure and should be considered into the fatigue failure.

Fatigue Design Criteria for Adhesively Bonded Anchorage for CFRP Tendon

Xie, Gui-Hua / Wang, C. M. / Xie, Fu-Zhe / Bian, Yu-Long

Abstract The fatigue failure criterion for the adhesively bonded anchorage system for CFRP (Carbon Fibre Reinforced Polymer) tendon has been investigated in this study. A closed-form shear stress solution was deduced for the static performance of the anchorage system, based on which the fatigue failure criterion was discussed and an analytical model was presented to judge the safety of the anchorage system under fatigue loading by using CLD (Constant Life Diagram) method. The results show that the Smith criterion is suitable for the analysis of fatigue failure occurred in the adhesively bonded anchorage system while the Goodman criterion may lead to risk. The stress concentration caused by manufacturing defects in the adhesively bonded anchorage system influences the occurrence of the fatigue failure and should be considered into the fatigue failure.

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

Fatigue Design Criteria for Adhesively Bonded Anchorage for CFRP Tendon

Beteiligte:

Xie, Gui-Hua (Autor:in) / Wang, C. M. (Autor:in) / Xie, Fu-Zhe (Autor:in) / Bian, Yu-Long (Autor:in)

Erschienen in:

ACMSM25 ; 373-384

Lecture Notes in Civil Engineering ; 37

Erscheinungsdatum:

04.09.2019

Format / Umfang:

12 pages

ISBN:

978-981-13-7602-3 , 978-981-13-7603-0

ISSN:

2366-2557 , 2366-2565

DOI:

https://doi.org/10.1007/978-981-13-7603-0_37

Medientyp:

Aufsatz/Kapitel (Buch)

Format:

Elektronische Ressource

Sprache:

Englisch

Schlagwörter:

Anchorage system , Fatigue failure criterion , FRP , Smith criterion , Goodman criterion Engineering , Civil Engineering , Structural Materials , Sustainable Architecture/Green Buildings , Theoretical and Applied Mechanics , Computer-Aided Engineering (CAD, CAE) and Design

Ähnliche Titel

Experimental study on fatigue performance of adhesively bonded anchorage system for CFRP tendons

Xie, Gui-hua / Tang, Yong-sheng / Wang, C.M. et al. | British Library Online Contents | 2018

Damage in adhesively bonded CFRP joints: Sinusoidal and impact-fatigue

Casas-Rodriguez, J. P. / Ashcroft, I. A. / Silberschmidt, V. V. | British Library Online Contents | 2008

Fatigue and creep analyses of adhesively bonded anchorages for CFRP tendons

Puigvert, F. / Crocombe, A.D. / Gil, L. | Tema Archiv | 2014

Dielectric studies of adhesively bonded CFRP/epoxy/CFRP structures - design for ageing

Halliday, S.T. / Banks, W.M. / Pethrick, R.A. | British Library Online Contents | 2000

Delamination in adhesively bonded CFRP joints: Standard fatigue, impact-fatigue and intermittent impact

Casas-Rodriguez, J. P. / Ashcroft, I. A. / Silberschmidt, V. V. | British Library Online Contents | 2008