MORTAR BASED ON ALKALI-ACTIVATED BLAST FURNACE SLAG

Microcracks formation as a result of the drying shrinkage process

Krizan, D. / Komljenovic, M.

Abstract Blast furnace slag was activated with water glass of different modulus n (mass ratio between SiO2and Na2O) and concentration. Linear deformations of alkali-activated slag mortar, i.e. mortar bars drying shrinkage, were examined as a function of the water glass modulus (n=0,6; 0,9; 1,2 and 1,5), water glass concentration (3 and 4% m/m calculated as Na2O) and slag specific surface area (430, 500 and 600m2/kg). Linear deformations of alkali-activated slag mortar were also compared with linear deformations of ordinary Portland cements mortar (CEM I 42.5).

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

MORTAR BASED ON ALKALI-ACTIVATED BLAST FURNACE SLAG

Microcracks formation as a result of the drying shrinkage process

Krizan, D. / Komljenovic, M.

Abstract Blast furnace slag was activated with water glass of different modulus n (mass ratio between SiO2and Na2O) and concentration. Linear deformations of alkali-activated slag mortar, i.e. mortar bars drying shrinkage, were examined as a function of the water glass modulus (n=0,6; 0,9; 1,2 and 1,5), water glass concentration (3 and 4% m/m calculated as Na2O) and slag specific surface area (430, 500 and 600m2/kg). Linear deformations of alkali-activated slag mortar were also compared with linear deformations of ordinary Portland cements mortar (CEM I 42.5).

MORTAR BASED ON ALKALI-ACTIVATED BLAST FURNACE SLAG

Microcracks formation as a result of the drying shrinkage process

Krizan, D. / Komljenovic, M.

Abstract Blast furnace slag was activated with water glass of different modulus n (mass ratio between SiO2and Na2O) and concentration. Linear deformations of alkali-activated slag mortar, i.e. mortar bars drying shrinkage, were examined as a function of the water glass modulus (n=0,6; 0,9; 1,2 and 1,5), water glass concentration (3 and 4% m/m calculated as Na2O) and slag specific surface area (430, 500 and 600m2/kg). Linear deformations of alkali-activated slag mortar were also compared with linear deformations of ordinary Portland cements mortar (CEM I 42.5).

Zugriff

Zugriff prüfen

Verfügbarkeit in meiner Bibliothek prüfen

Bestellung bei Subito €

Seitennavigation

Dokumentinformationen

Ähnliche Titel

Exportieren, teilen und zitieren

Dokumentinformationen

Titel:

MORTAR BASED ON ALKALI-ACTIVATED BLAST FURNACE SLAG

Untertitel:

Microcracks formation as a result of the drying shrinkage process

Beteiligte:

Krizan, D. (Autor:in) / Komljenovic, M. (Autor:in)

Erschienen in:

Measuring, Monitoring and Modeling Concrete Properties ; 361-366

Erscheinungsdatum:

01.01.2006

Format / Umfang:

6 pages

ISBN:

978-1-4020-5104-3 , 978-1-4020-5103-6

DOI:

https://doi.org/10.1007/978-1-4020-5104-3_43

Medientyp:

Aufsatz/Kapitel (Buch)

Format:

Elektronische Ressource

Sprache:

Englisch

Schlagwörter:

Portland Cement , Ordinary Portland Cement , Blast Furnace Slag , Calcium Silicate Hydrate , Water Glass Engineering , Building Materials

Ähnliche Titel

Mortar Based on Alkali-Activated Blast Furnace Slag

Krizan, D. / Komljenovic, M. | British Library Conference Proceedings | 2006

Carbonation Characteristics of Alkali-Activated Blast-Furnace Slag Mortar

Song, Keum-Il / Song, Jin-Kyu / Lee, Bang-Yeon et al. | Tema Archiv | 2014

Carbonation resistance of calcined clay-ground granulated blast furnace slag alkali-activated mortar

Gomes, Samuel De Carvalho / Nguyen, Quang Dieu / Li, Wengui et al. | Elsevier | 2023

Suitability of commercial superplasticizers for one-part alkali-activated blast-furnace slag mortar

Luukkonen, Tero / Abdollahnejad, Zahra / Ohenoja, Katja et al. | Taylor & Francis Verlag | 2019

Characterization of ferrochrome ash and blast furnace slag based alkali-activated paste and mortar

Omur, Tarik / Miyan, Nausad / Kabay, Nihat et al. | Elsevier | 2022