On the influence of repetitive corrugation and straightening on the microstructure and mechanical properties of AA 8090 Al-Li alloy
This paper reports on the improvements in the mechanical properties of AA8090 Al-Li alloy subjected to repetitive corrugation and straightening (RCS). AA 8090 Al-Li alloy sheets were processed using different corrugation profiles (semi-circular, flat-groove and V-groove) at 300 °C, with a pressing velocity of 2.5 mm/s. This study shows that a V-grooved die favors grain refinement, e.g. a reduction in the average grain size from 65 μm to 12 μm after eight passes is achieved. Grain size distribution and misorientation between grain boundaries were studied using EBSD and TEM. The microstructures also appear to have more high-angle grain boundaries in the case of the specimen processed using the V-grooved die. The tensile strength increases with the number of passes, but drops when surface cracks appear after the 16th pass for a semi-circular die, the 12th pass for a flat grooved die and the 10th pass for a V-grooved die. In contrast, the hardness continues to increase with increasing number of passes. Ultra-fine-/nano-grains were present after the eighth pass in a sheet that was processed using a V-grooved die.
On the influence of repetitive corrugation and straightening on the microstructure and mechanical properties of AA 8090 Al-Li alloy
This paper reports on the improvements in the mechanical properties of AA8090 Al-Li alloy subjected to repetitive corrugation and straightening (RCS). AA 8090 Al-Li alloy sheets were processed using different corrugation profiles (semi-circular, flat-groove and V-groove) at 300 °C, with a pressing velocity of 2.5 mm/s. This study shows that a V-grooved die favors grain refinement, e.g. a reduction in the average grain size from 65 μm to 12 μm after eight passes is achieved. Grain size distribution and misorientation between grain boundaries were studied using EBSD and TEM. The microstructures also appear to have more high-angle grain boundaries in the case of the specimen processed using the V-grooved die. The tensile strength increases with the number of passes, but drops when surface cracks appear after the 16th pass for a semi-circular die, the 12th pass for a flat grooved die and the 10th pass for a V-grooved die. In contrast, the hardness continues to increase with increasing number of passes. Ultra-fine-/nano-grains were present after the eighth pass in a sheet that was processed using a V-grooved die.
On the influence of repetitive corrugation and straightening on the microstructure and mechanical properties of AA 8090 Al-Li alloy
Archiv.Civ.Mech.Eng
Jenix Rino, J (Autor:in) / Balasivanandha Prabu, S (Autor:in) / Padmanabhan, K. A (Autor:in)
Archives of Civil and Mechanical Engineering ; 18 ; 280-290
01.03.2018
11 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| British Library Online Contents | 2018
Development of repetitive corrugation and straightening
| British Library Online Contents | 2004
Effect of repetitive corrugation and straightening on Al and Al–0.25Sc alloy
| British Library Online Contents | 2008
| British Library Online Contents | 2011
| British Library Online Contents | 2012