Effect of very fine aggregate on concrete strength
Abstract The effect of very fine aggregate on the water requirement and strength evolution of superplasticized concrete was studied. The maximum aggregate size was 6 mm, fine aggregate content 0–15% of the total aggregate, binder (OPC and silica) content 80–800 kg m−3, and specific surface area of the finest aggregate material 18–1000 m2 kg−1. The water requirement for constant workability fell sharply with increasing amount and fineness of the very fine aggregate due to improved particle packing. At constant, relatively small binder contents of 80–250 kg m−3, modifying the aggregate distribution increased the 91-day strength of 6 mm concrete as much as threefold, e.g. from 20 to 65 MPa at 200 kg m−3. This effect was less significant the greater the binder content. The correlation between strength and porosity was similar regardless of concrete composition. The stress-strain behaviour was more dependent on strength than on composition
Resume On a étudié l'effet d'un granulat très fin sur le besion en eau et l'évolution de la résistance d'un béton traité aux superplastifiants. La taille maximale du granulat était de 6 mm, la teneur en granulat fin de 0 à 15% de la quantité de granulat totale, la teneur en liant (OPC et silice) de 80–800 kg m−3 et la surface spécifique du plus fin granulat de 18–1000 m2 kg−1. Le besoin en eau pour une ouvrabilité constante a nettement diminué lorsque la quantité et la finesse du granulat ont augmenté en raison de l'amélioration de la compacité des particules. Pour des teneurs en liant constantes, relativement faibles, de 80–250 kg m−3, en modifiant la distribution du granulat, la résistance à 91 jours du mélange de béton de 6 mm s'est accrue jusqu'à trois fois, soit de 20–65 MPa pour 200 kg m−3. Plus la teneur en liant était élevée, moins cet effect a été significatif. La corrélation entre la résistance et la porosité ne dépend pas de la composition du béton. L'état du béton sous contrainte/déformation dépend davantage de la résistance que de la composition.
Effect of very fine aggregate on concrete strength
Abstract The effect of very fine aggregate on the water requirement and strength evolution of superplasticized concrete was studied. The maximum aggregate size was 6 mm, fine aggregate content 0–15% of the total aggregate, binder (OPC and silica) content 80–800 kg m−3, and specific surface area of the finest aggregate material 18–1000 m2 kg−1. The water requirement for constant workability fell sharply with increasing amount and fineness of the very fine aggregate due to improved particle packing. At constant, relatively small binder contents of 80–250 kg m−3, modifying the aggregate distribution increased the 91-day strength of 6 mm concrete as much as threefold, e.g. from 20 to 65 MPa at 200 kg m−3. This effect was less significant the greater the binder content. The correlation between strength and porosity was similar regardless of concrete composition. The stress-strain behaviour was more dependent on strength than on composition
Resume On a étudié l'effet d'un granulat très fin sur le besion en eau et l'évolution de la résistance d'un béton traité aux superplastifiants. La taille maximale du granulat était de 6 mm, la teneur en granulat fin de 0 à 15% de la quantité de granulat totale, la teneur en liant (OPC et silice) de 80–800 kg m−3 et la surface spécifique du plus fin granulat de 18–1000 m2 kg−1. Le besoin en eau pour une ouvrabilité constante a nettement diminué lorsque la quantité et la finesse du granulat ont augmenté en raison de l'amélioration de la compacité des particules. Pour des teneurs en liant constantes, relativement faibles, de 80–250 kg m−3, en modifiant la distribution du granulat, la résistance à 91 jours du mélange de béton de 6 mm s'est accrue jusqu'à trois fois, soit de 20–65 MPa pour 200 kg m−3. Plus la teneur en liant était élevée, moins cet effect a été significatif. La corrélation entre la résistance et la porosité ne dépend pas de la composition du béton. L'état du béton sous contrainte/déformation dépend davantage de la résistance que de la composition.
Effect of very fine aggregate on concrete strength
Kronlöf, A. (Autor:in)
Materials and Structures ; 27 ; 15-25
01.01.1994
11 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Effect of very fine aggregate on concrete strength
| Online Contents | 1994
Effect of very fine aggregate on concrete strength
| British Library Online Contents | 1994
The strength of fine-aggregate concrete
| Engineering Index Backfile | 1918
High-strength concrete with different fine aggregate
| Online Contents | 2002