Laser Surface Alloying of Aluminum for Improving Acid Corrosion Resistance
Abstract In the present study, laser surface alloying of aluminum with magnesium, manganese, titanium and zinc, respectively, was carried out to improve acid corrosion resistance. Laser surface alloying was conducted using 1600 and 1800 W power source using CO2 laser. Acid corrosion resistance was tested by dipping the samples in a solution of 2.5% H2SO4 for 200 h. The weight loss due to acid corrosion was reduced by 55% for AlTi, 41% for AlMg alloy, 36% for AlZn and 22% for AlMn alloy. Laser surface alloyed samples offered greater corrosion resistance than the aluminum substrate. It was observed that localized pitting corrosion was the major factor to damage the surface when exposed for a long time. The hardness after laser surface alloying was increased by a factor of 8.7, 3.4, 2.7 and 2 by alloying with Mn, Mg, Ti and Zn, respectively. After corrosion test, hardness was reduced by 51% for AlTi sample, 40% for AlMg sample, 41.4% for AlMn sample and 33% for AlZn sample.
Laser Surface Alloying of Aluminum for Improving Acid Corrosion Resistance
Abstract In the present study, laser surface alloying of aluminum with magnesium, manganese, titanium and zinc, respectively, was carried out to improve acid corrosion resistance. Laser surface alloying was conducted using 1600 and 1800 W power source using CO2 laser. Acid corrosion resistance was tested by dipping the samples in a solution of 2.5% H2SO4 for 200 h. The weight loss due to acid corrosion was reduced by 55% for AlTi, 41% for AlMg alloy, 36% for AlZn and 22% for AlMn alloy. Laser surface alloyed samples offered greater corrosion resistance than the aluminum substrate. It was observed that localized pitting corrosion was the major factor to damage the surface when exposed for a long time. The hardness after laser surface alloying was increased by a factor of 8.7, 3.4, 2.7 and 2 by alloying with Mn, Mg, Ti and Zn, respectively. After corrosion test, hardness was reduced by 51% for AlTi sample, 40% for AlMg sample, 41.4% for AlMn sample and 33% for AlZn sample.
Laser Surface Alloying of Aluminum for Improving Acid Corrosion Resistance
Jiru, Woldetinsay Gutu (Autor:in) / Sankar, Mamilla Ravi (Autor:in) / Dixit, Uday Shanker (Autor:in)
Journal of The Institution of Engineers (India): Series C ; 100 ; 481-492
09.04.2018
12 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Laser Surface Alloying of Aluminum for Improving Acid Corrosion Resistance
| Online Contents | 2019
| British Library Online Contents | 1998
Improving Corrosion Resistance of Magnesium by Nonequilibrium Alloying with Yttrium
| British Library Online Contents | 1993
Laser Surface Alloying of Aluminium 2014 Alloy With Mo for Enhanced Corrosion Resistance
| Springer Verlag | 1996
Improving the wear resistance of AA 6061 by laser surface alloying with NiTi
| British Library Online Contents | 2007