Waste printed circuit boards nonmetallic powder as admixture in cement mortar
Abstract In this paper, the nonmetallic powder recycled from waste printed circuit boards (PCBs) is used in cement mortar as admixture. The mechanical properties, bulk density, air content, water-retention property, shrinkage rate and water capillary adsorption are tested. The results show that the waste PCBs nonmetallic powder causes an increase in air content and improves the water-retention property of fresh mortar, decreases the bulk density of hardened mortar. The compressive strength and flexural strength of mortar with PCBs nonmetallic powder change slightly with the m p/m c below 15%. The tensile bond strength goes down continuously with the increase of the m p/m c but the reducing trend in the m p/m c range from 0 to 10% is slow. The drying shrinkage rate of mortar has little change as the m p/m c varies from 0 to 15%. The water capillary adsorption of mortar with the m p/m c of 5, 10 and 15% are lower than that of control. Cement mortar made with recycled waste PCBs nonmetallic powder is a new type of green building materials, which is friendly to environment and has broad application prospects.
Waste printed circuit boards nonmetallic powder as admixture in cement mortar
Abstract In this paper, the nonmetallic powder recycled from waste printed circuit boards (PCBs) is used in cement mortar as admixture. The mechanical properties, bulk density, air content, water-retention property, shrinkage rate and water capillary adsorption are tested. The results show that the waste PCBs nonmetallic powder causes an increase in air content and improves the water-retention property of fresh mortar, decreases the bulk density of hardened mortar. The compressive strength and flexural strength of mortar with PCBs nonmetallic powder change slightly with the m p/m c below 15%. The tensile bond strength goes down continuously with the increase of the m p/m c but the reducing trend in the m p/m c range from 0 to 10% is slow. The drying shrinkage rate of mortar has little change as the m p/m c varies from 0 to 15%. The water capillary adsorption of mortar with the m p/m c of 5, 10 and 15% are lower than that of control. Cement mortar made with recycled waste PCBs nonmetallic powder is a new type of green building materials, which is friendly to environment and has broad application prospects.
Waste printed circuit boards nonmetallic powder as admixture in cement mortar
Wang, Ru (Autor:in) / Zhang, Tengfei (Autor:in) / Wang, Peiming (Autor:in)
Materials and Structures ; 45 ; 1439-1445
07.02.2012
7 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Waste printed circuit boards , Nonmetallic powder , Cement mortar , Strengths , Shrinkage rate , Water capillary adsorption Engineering , Theoretical and Applied Mechanics , Operating Procedures, Materials Treatment , Materials Science, general , Structural Mechanics , Building Materials , Civil Engineering
Waste printed circuit boards nonmetallic powder as admixture in cement mortar
| Online Contents | 2012
Waste printed circuit boards nonmetallic powder as admixture in cement mortar
| Online Contents | 2012
Waste printed circuit boards nonmetallic powder as admixture in cement mortar
| British Library Online Contents | 2012
Waste printed circuit boards nonmetallic powder as admixture in cement mortar
| Online Contents | 2012
Europäisches Patentamt | 2021