Microstructural Characterizations with EDAX Analysis of Dissimilar Friction Stir Welds
Abstract This paper reports the microstructural characteristics of dissimilar friction stir welds with AA7075T651 and AA6061T651. Dissimilar friction stir welds between AA7075T651 and AA6061T651 were produced by varying the rotational speeds between 800 and 1,000 rpm and the welding speeds between 90 and 110 mm/min. The welds were characterized through optical microscope and scanning electron microscope (SEM). Three different tool profiles (taper cylindrical threaded, taper square threaded and simple square) were used for this investigation and in that taper cylindrical threaded tool with process parameters 900 rpm and 100 mm/min were found to have maximum tensile strength of 205 MPa for the dissimilar butt joints. The SEM with energy-dispersive X-ray spectroscopy analysis reveals the metallurgical bonding achieved at the joint interfaces of the welds produced. The good mixing of both the materials joined was obtained at lower welding and higher rotational speed while the tunnel defect was found to be common in the welds produced irrespective of the tool pin profiles and process parameters due to insufficient axial load with 0° tilt angle.
Microstructural Characterizations with EDAX Analysis of Dissimilar Friction Stir Welds
Abstract This paper reports the microstructural characteristics of dissimilar friction stir welds with AA7075T651 and AA6061T651. Dissimilar friction stir welds between AA7075T651 and AA6061T651 were produced by varying the rotational speeds between 800 and 1,000 rpm and the welding speeds between 90 and 110 mm/min. The welds were characterized through optical microscope and scanning electron microscope (SEM). Three different tool profiles (taper cylindrical threaded, taper square threaded and simple square) were used for this investigation and in that taper cylindrical threaded tool with process parameters 900 rpm and 100 mm/min were found to have maximum tensile strength of 205 MPa for the dissimilar butt joints. The SEM with energy-dispersive X-ray spectroscopy analysis reveals the metallurgical bonding achieved at the joint interfaces of the welds produced. The good mixing of both the materials joined was obtained at lower welding and higher rotational speed while the tunnel defect was found to be common in the welds produced irrespective of the tool pin profiles and process parameters due to insufficient axial load with 0° tilt angle.
Microstructural Characterizations with EDAX Analysis of Dissimilar Friction Stir Welds
Ravikumar, S. (Autor:in) / Rao, V. S. (Autor:in)
Journal of The Institution of Engineers (India): Series C ; 94 ; 307-315
01.10.2013
9 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Microstructural Characterizations with EDAX Analysis of Dissimilar Friction Stir Welds
| Online Contents | 2013
Microstructure, residual strain, and eigenstrain analysis of dissimilar friction stir welds
| British Library Online Contents | 2010
| British Library Online Contents | 2011