Means for protecting underwater structures at the Tsimlyansk hydroelectric stations from fouling by mussels: Fid-Bau Portal

Means for protecting underwater structures at the Tsimlyansk hydroelectric stations from fouling by mussels

Luchina, M. A. / Malysheva, T. I. / Frost, E. I. / Sinel'nikova, N. R. / Kazakov, M. I.

Conclusions 1. The abundant mussel fouling of the surfaces of the trash racks, gates of the dam and turbines, concrete scroll cases of the units, and technical water supply system at the Tsimlyansk station results from the favorable physicochemical conditions for development of the mussel. During the season the fouling biomass reaches 11–12 kg/m2. 2. Industrially produced antifouling enamels KhS-522, KhS-79 blue, KhV-53, and KF-751 can be used to protect underwater structures from fouling by mussels. Paints with organotin toxins KhS-521 with TBTO, KhS-519, KhS-519 r. 23, and Kch-520 are also promising, but need further testing. 3. Antifouling enamels should be applied on stable anticorrosion coatings on a vinyl (KhS-720, KhV-74) and epoxy (ÉP-44) base, and also on coatings on a base of enamels KhS-416, KhS-413, etc. 4. Metal structures can be protected against mussel fouling by cathodic means with constant polarization at current densities of 0.4–0.8 A/m2. 5. It was established for the first time that complete protection from fouling is possible with periodic polarization once every 10 days for 8 h at a current density of 4 A/m2. This regime should be maintained for 3–4.5 months a year at the time of intense fouling. 6. The possibility of using antifouling coatings along with cathodic protection from corrosion was investigated. It was established that enamel KhS-522 operating with polarization by a current density of 0.02–0.06 A/m2 for 2 years completely retained its antifouling properties and did not show any traces of damage.