The specific surface area of hydrated cement obtained from permeability data
Abstract Old data on the permeability to water of cement pastes were reanalyzed. Findings: the coefficient of permeability of cement paste is a relatively simple function of: 1) capacity for evaporable water, i.e., porosity; 2) the specific surface area of the solid matter in the paste; 3) the coefficient of viscous resistance. The latter is a known function, evaluated empirically, of the free energy of activation for flow which is a function of porosity and temperature. Total energy (enthalpy) of activation for flow through paste, and entropy, were evaluated. The water that flows is identical with the total evaporable water as defined by Powers and Brownyard, or nearly so. The specific surface of completely hydrate cement as derived from virgin paste by the permeability method is about 30% larger than the figure from water-vapor adsorption on once-dried material by the BET method.
Résumé Toutes les données sur la perméabilité dans les pates de ciment qui ont fait l'objet d'une nouvelle analyse montrent que le coefficient de perméabilité de la pâte de ciment est une fonction relativement simple de: 1) la capacité d'eau évaporable, c'est-à-dire la porosité; 2) la surface spécifique totale de la matière solide de la pâte; 3) du coefficient de frottement visqueux. Ce dernier est une fonction connue que l'on évalue ampiriquement de l'énergie libre d'activation pour un écoulement qui est une fonction de la porosité et de la température. On a évalué l'énergie totale (enthalpie) d'activation pour lécoulement à travers la pâte et l'entropie. L'eau qui s'écoule est identique ou peu s'en faut à l'eau évaporable totale selon la définition donnée par Powers et Brownyard. La surface spécifique du ciment complètement hydraté telle qu'on l'obtient d'après la perméabilité de la pâte vierge est d'environ 30% supéreure à la valeur obtenue par la méthode BET (adsorption eau/vapeur sur le matériau séché).
The specific surface area of hydrated cement obtained from permeability data
Abstract Old data on the permeability to water of cement pastes were reanalyzed. Findings: the coefficient of permeability of cement paste is a relatively simple function of: 1) capacity for evaporable water, i.e., porosity; 2) the specific surface area of the solid matter in the paste; 3) the coefficient of viscous resistance. The latter is a known function, evaluated empirically, of the free energy of activation for flow which is a function of porosity and temperature. Total energy (enthalpy) of activation for flow through paste, and entropy, were evaluated. The water that flows is identical with the total evaporable water as defined by Powers and Brownyard, or nearly so. The specific surface of completely hydrate cement as derived from virgin paste by the permeability method is about 30% larger than the figure from water-vapor adsorption on once-dried material by the BET method.
Résumé Toutes les données sur la perméabilité dans les pates de ciment qui ont fait l'objet d'une nouvelle analyse montrent que le coefficient de perméabilité de la pâte de ciment est une fonction relativement simple de: 1) la capacité d'eau évaporable, c'est-à-dire la porosité; 2) la surface spécifique totale de la matière solide de la pâte; 3) du coefficient de frottement visqueux. Ce dernier est une fonction connue que l'on évalue ampiriquement de l'énergie libre d'activation pour un écoulement qui est une fonction de la porosité et de la température. On a évalué l'énergie totale (enthalpie) d'activation pour lécoulement à travers la pâte et l'entropie. L'eau qui s'écoule est identique ou peu s'en faut à l'eau évaporable totale selon la définition donnée par Powers et Brownyard. La surface spécifique du ciment complètement hydraté telle qu'on l'obtient d'après la perméabilité de la pâte vierge est d'environ 30% supéreure à la valeur obtenue par la méthode BET (adsorption eau/vapeur sur le matériau séché).
The specific surface area of hydrated cement obtained from permeability data
Powers, T. C. (Autor:in)
Matériaux et Construction ; 12 ; 159-168
01.05.1979
10 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Surface area of hydrated Portland cement
| Engineering Index Backfile | 1950
The BET-specific surface area of hydrated Portland cement and related materials
| British Library Online Contents | 2003
The BET-specific surface area of hydrated Portland cement and related materials
| Tema Archiv | 2003
The BET-specific surface area of hydrated Portland cement and related materials
| Online Contents | 2003