Modeling and empirical formulas for chemical corrosion and stress corrosion of cementitious materials
Abssract The behavior of mortar, ordinary concrete and high strength concrete under chemical corrosion and stress corrosion attacks is studied in the presented work. The specimens were immersed into a variety of chemical solutions, namely, 5% and 0.5% ammonium sulfate solutions, 10% and 1% ammonium nitrate solutions, and under different flexural loads with load levels of 30%, 40% and 50% of their initial flexural strengths, respectively. The strength development of the specimens was studied. The depth of penetration of the attacking ammonium nitrate ions was also determined. A synergy effect factor which describes the simultaneous actions of mechanical stresses and chemical attacks is defined in this paper. Consequently, a strength model for cementitious materials was developed, and new equations describing chemical corrosion and stress corrosion of cementitious materials,i.e. strength-time-curves, are proposed.
Résumé Le comportement du mortier, du béton ordinaire et du béton à haute résistance sous l'effet agressif de la corrosion chimique et de la corrosion due à la contrainte est étudié dans le présent article. Les échantillons ont été respectivement immergés dans diverses solutions chimiques, à savoir des solutions de sulfate d'ammonium à 5% et à 0,5%, des solutions de nitrate d'ammonium à 10% et à 1%, et ont été soumis à des charges en flexion de niveau de 30%, 40% et de 50% de la résistance de la flexion initiale. L'évolution de la résistance des échantillons a été étudiée ainsi que le taux de pénétration des ions de nitrate d'ammonium. Un facteur d'effet synergique décrivant l'action simultanée des contraintes mécaniques et d'agressions chimiques, est défini dans cet article. Ainsi, un modèle de la résistance pour des matériaux à base de ciment a été élaboré et des nouvelles équations concernant la corrosion chimique ainsi que la corrosion due à la contrainte des matériaux à base de ciment, c'est-à-dire la courbe résistance-temps, sont ensuite proposées.
Modeling and empirical formulas for chemical corrosion and stress corrosion of cementitious materials
Abssract The behavior of mortar, ordinary concrete and high strength concrete under chemical corrosion and stress corrosion attacks is studied in the presented work. The specimens were immersed into a variety of chemical solutions, namely, 5% and 0.5% ammonium sulfate solutions, 10% and 1% ammonium nitrate solutions, and under different flexural loads with load levels of 30%, 40% and 50% of their initial flexural strengths, respectively. The strength development of the specimens was studied. The depth of penetration of the attacking ammonium nitrate ions was also determined. A synergy effect factor which describes the simultaneous actions of mechanical stresses and chemical attacks is defined in this paper. Consequently, a strength model for cementitious materials was developed, and new equations describing chemical corrosion and stress corrosion of cementitious materials,i.e. strength-time-curves, are proposed.
Résumé Le comportement du mortier, du béton ordinaire et du béton à haute résistance sous l'effet agressif de la corrosion chimique et de la corrosion due à la contrainte est étudié dans le présent article. Les échantillons ont été respectivement immergés dans diverses solutions chimiques, à savoir des solutions de sulfate d'ammonium à 5% et à 0,5%, des solutions de nitrate d'ammonium à 10% et à 1%, et ont été soumis à des charges en flexion de niveau de 30%, 40% et de 50% de la résistance de la flexion initiale. L'évolution de la résistance des échantillons a été étudiée ainsi que le taux de pénétration des ions de nitrate d'ammonium. Un facteur d'effet synergique décrivant l'action simultanée des contraintes mécaniques et d'agressions chimiques, est défini dans cet article. Ainsi, un modèle de la résistance pour des matériaux à base de ciment a été élaboré et des nouvelles équations concernant la corrosion chimique ainsi que la corrosion due à la contrainte des matériaux à base de ciment, c'est-à-dire la courbe résistance-temps, sont ensuite proposées.
Modeling and empirical formulas for chemical corrosion and stress corrosion of cementitious materials
Schneider, U. (Autor:in) / Chen, S. -W. (Autor:in)
Materials and Structures ; 31 ; 662-668
01.12.1998
7 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
| British Library Online Contents | 1998
Stress corrosion of cementitious materials in sulphate solutions
| Online Contents | 1990
Stress corrosion of cementitious materials in sulphate solutions
| Springer Verlag | 1990