Wear and Corrosion Behavior of CoNiCrAlY Bond Coats
Abstract The present study focusses on the wear and microstructural properties of CoNiCrAlY coatings fabricated on AISI 316L stainless steel substrate by using the (HVOF) and (CGDS) methods. A triobiological test was performed on the samples in order to understand the wear behaviour of thermally sprayed coatings. The microstructures of as-sprayed and worn out coatings were investigated by scanning electron microscopy. Coating hardness measurements were performed with nanoindentation. HVOF coating revealed lower hardness value in comparison with CGDS. Studies depicted better wear resistance of the CGDS sprayed with He, when compared to CGDS N2 and HVOF processing. Potentiodynamic polarization curves and tafel extrapolation experiments were carried at 7.5 pH value using 3.5 % NaCl as an electrolyte. Electrochemical studies depicted better corrosion resistance of the He processed coating when compared to N2 and HVOF processing.
Wear and Corrosion Behavior of CoNiCrAlY Bond Coats
Abstract The present study focusses on the wear and microstructural properties of CoNiCrAlY coatings fabricated on AISI 316L stainless steel substrate by using the (HVOF) and (CGDS) methods. A triobiological test was performed on the samples in order to understand the wear behaviour of thermally sprayed coatings. The microstructures of as-sprayed and worn out coatings were investigated by scanning electron microscopy. Coating hardness measurements were performed with nanoindentation. HVOF coating revealed lower hardness value in comparison with CGDS. Studies depicted better wear resistance of the CGDS sprayed with He, when compared to CGDS N2 and HVOF processing. Potentiodynamic polarization curves and tafel extrapolation experiments were carried at 7.5 pH value using 3.5 % NaCl as an electrolyte. Electrochemical studies depicted better corrosion resistance of the He processed coating when compared to N2 and HVOF processing.
Wear and Corrosion Behavior of CoNiCrAlY Bond Coats
Rathod, W. S. (Autor:in) / Khanna, A. S. (Autor:in) / Rathod, R. C. (Autor:in) / Sapate, S. G. (Autor:in)
Journal of The Institution of Engineers (India): Series C ; 95 ; 261-271
01.07.2014
11 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Wear and Corrosion Behavior of CoNiCrAlY Bond Coats
| Online Contents | 2014
Bioxidant corrosion behaviour of CoNiCrAlY coated IN738 at 1100 °C
| British Library Online Contents | 2019
| British Library Online Contents | 2006
Application of small punch creep testing to a thermally sprayed CoNiCrAlY bond coat
| British Library Online Contents | 2013