A Numerical Study of the Tensile Stress Concentration in a Hemi-ellipsoidal Corrosion Pit on a Plate
Abstract Fatigue cracks initiated from corrosion pits have been reported in various metallic structures under corrosive environments. Pit-to-crack transition occurs when the stress conditions around a corrosion pit exceed the endurance limit of the material. The effect of stress concentration at the site of a hemi-ellipsoidal corrosion pit on a metal plate was investigated using rigorous finite element analysis. Pit configuration and plate thickness were major parameters determining stress concentration factors (SCFs). Pit configuration and plate thickness were parameterized and the effects of each as a SCF were investigated. An increasing monotonic trend was evident as the pit became narrower and deeper. The effect of pit configuration was negligible, however, when the pit depth approached the plate thickness. Based on variations in the SCFs, parametric equations were developed via nonlinear regression analysis. The equations aptly represented each of the parameter characteristics and were used to accurately estimate their effect as a SCF.
A Numerical Study of the Tensile Stress Concentration in a Hemi-ellipsoidal Corrosion Pit on a Plate
Abstract Fatigue cracks initiated from corrosion pits have been reported in various metallic structures under corrosive environments. Pit-to-crack transition occurs when the stress conditions around a corrosion pit exceed the endurance limit of the material. The effect of stress concentration at the site of a hemi-ellipsoidal corrosion pit on a metal plate was investigated using rigorous finite element analysis. Pit configuration and plate thickness were major parameters determining stress concentration factors (SCFs). Pit configuration and plate thickness were parameterized and the effects of each as a SCF were investigated. An increasing monotonic trend was evident as the pit became narrower and deeper. The effect of pit configuration was negligible, however, when the pit depth approached the plate thickness. Based on variations in the SCFs, parametric equations were developed via nonlinear regression analysis. The equations aptly represented each of the parameter characteristics and were used to accurately estimate their effect as a SCF.
A Numerical Study of the Tensile Stress Concentration in a Hemi-ellipsoidal Corrosion Pit on a Plate
An, Lee-Sak (Autor:in) / Park, Yeun Chul (Autor:in) / Kim, Ho-Kyung (Autor:in)
International Journal of Steel Structures ; 19 ; 530-542
02.08.2018
13 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
A Numerical Study of the Tensile Stress Concentration in a Hemi-ellipsoidal Corrosion Pit on a Plate
| Online Contents | 2018
Stress concentration factors of a general triaxial ellipsoidal cavity
| British Library Online Contents | 2008
Stress Concentration near an Elastic Ellipsoidal Inclusion in an Infinite Body
| British Library Online Contents | 2002