Influence of pitting corrosion parameters on the residual fatigue life of a steel cable
Corrosion wastage is a significant factor that leads to load bearing capacity degradation of cable steel wire (CSW) structures. This paper aims to study the influence of pitting corrosion parameters on residual fatigue life (RFL) of a steel cable, so as to fit a series of formulas to predict the RFL of steel cables directly and quickly. Firstly, single and double pitting corroded CSWs are modelled by FEM. Secondly, stress concentration factors (SCFs) and residual fatigue lives (RFLs) of the corroded CSWs are calculated. Finally, calculation formulas of SCFs and RFLs of the CSWs with various pit depths and widths are fitted. The results show that SCF increases with the increase of pit depth and decreases with the increase of pit width. RFL decreases with the increase of pit depth and increases with the increase of pit width. SCF and RFL have nothing to do with the amount of corrosion pits, but only affected by the depth of the deepest pit.
Influence of pitting corrosion parameters on the residual fatigue life of a steel cable
Corrosion wastage is a significant factor that leads to load bearing capacity degradation of cable steel wire (CSW) structures. This paper aims to study the influence of pitting corrosion parameters on residual fatigue life (RFL) of a steel cable, so as to fit a series of formulas to predict the RFL of steel cables directly and quickly. Firstly, single and double pitting corroded CSWs are modelled by FEM. Secondly, stress concentration factors (SCFs) and residual fatigue lives (RFLs) of the corroded CSWs are calculated. Finally, calculation formulas of SCFs and RFLs of the CSWs with various pit depths and widths are fitted. The results show that SCF increases with the increase of pit depth and decreases with the increase of pit width. RFL decreases with the increase of pit depth and increases with the increase of pit width. SCF and RFL have nothing to do with the amount of corrosion pits, but only affected by the depth of the deepest pit.
Influence of pitting corrosion parameters on the residual fatigue life of a steel cable
Cai, Long (Autor:in) / Zhang, Wei (Autor:in) / Long, Zhilin (Autor:in) / Liu, Zhengcai (Autor:in)
Australian Journal of Structural Engineering ; 24 ; 310-323
02.10.2023
14 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
The effect of pitting corrosion on fatigue life
| British Library Online Contents | 2000
Effect of pitting corrosion on fatigue crack initiation and fatigue life
| British Library Online Contents | 1999
Pitting Corrosion and Fatigue Behavior
| British Library Online Contents | 2000
Influence of pitting on the fatigue life of a turbine blade steel
| British Library Online Contents | 1999
Damage tolerance approach for probabilistic pitting corrosion fatigue life prediction
| British Library Online Contents | 2001