Section loss in naturally corroded 7-wire steel strands in external tendons
Naturally corroded seven-wire strands obtained from two in-service bridges were examined. All strand samples were cut into cross sections, and the corrosion depths and corroded areas were measured. Among various corrosion mechanisms, a majority of samples investigated were categorized as general corrosion. The trends in the section losses in the strands with respect to average corrosion depth were similar and showed a clear linearity. The average corrosion depth measured from the outside of strands showed an overall linear trend with section loss when the inside of strand cross-sections could not be observed and measured. In this study, a method to estimate section loss for general corrosion of a 7-wire strand is developed by using corrosion depth in the visible region. Although a limited number of samples were obtained from only two bridges, the section loss estimates were comparable to actual measurements. The study of strand samples corroded during service offers a rare opportunity and should distinguish this study from previous ones.
Section loss in naturally corroded 7-wire steel strands in external tendons
Naturally corroded seven-wire strands obtained from two in-service bridges were examined. All strand samples were cut into cross sections, and the corrosion depths and corroded areas were measured. Among various corrosion mechanisms, a majority of samples investigated were categorized as general corrosion. The trends in the section losses in the strands with respect to average corrosion depth were similar and showed a clear linearity. The average corrosion depth measured from the outside of strands showed an overall linear trend with section loss when the inside of strand cross-sections could not be observed and measured. In this study, a method to estimate section loss for general corrosion of a 7-wire strand is developed by using corrosion depth in the visible region. Although a limited number of samples were obtained from only two bridges, the section loss estimates were comparable to actual measurements. The study of strand samples corroded during service offers a rare opportunity and should distinguish this study from previous ones.
Section loss in naturally corroded 7-wire steel strands in external tendons
Yoo, Chul-Hwan (Autor:in) / Park, Yeun Chul (Autor:in) / Kim, Ho-Kyung (Autor:in)
Structure and Infrastructure Engineering ; 16 ; 1593-1603
01.11.2020
11 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Strength reduction curves for corroded seven‐wire strands
| Wiley | 2023
Strength reduction curves for corroded seven‐wire strands
| Wiley | 2023
Corroded post-tensioned beams with bonded tendons and wire failure
| Online Contents | 2009
Corroded post-tensioned beams with bonded tendons and wire failure
| Online Contents | 2009