Boron ores are used in the production of various boron compounds such as boric acid, borax and boron oxide. Boric acid is produced by reacting colemanite(2CaO dot 3B2O3 dot 5H2O) with sulphuric acid and a large quantity of borogypsum is formed during this production. This waste causes various environmental problems when discharged directly to the environment. Portland cement is the most important material in the building industry. This material is produced by adding about 3-5% gypsum (CaSO4 dot 2H2O) to clinker as a set retarder. The aim of this study was to stabilize borogypsum, and to produce cements by adding borogypsum instead of natural gypsum to clinker. Concrete using cement produced with borogypsum was tested to find the mechanical properties and the test values were compared with those of concrete from cement with natural gypsum. Compressive strength of concrete from cement produced with borogypsum was found to be higher than that of natural gypsum. Also, the setting time of cement with borogypsum was longer than that of the Portland cement.
Utilization of borogypsum as set retarder in Portland cement production
Boron ores are used in the production of various boron compounds such as boric acid, borax and boron oxide. Boric acid is produced by reacting colemanite(2CaO dot 3B2O3 dot 5H2O) with sulphuric acid and a large quantity of borogypsum is formed during this production. This waste causes various environmental problems when discharged directly to the environment. Portland cement is the most important material in the building industry. This material is produced by adding about 3-5% gypsum (CaSO4 dot 2H2O) to clinker as a set retarder. The aim of this study was to stabilize borogypsum, and to produce cements by adding borogypsum instead of natural gypsum to clinker. Concrete using cement produced with borogypsum was tested to find the mechanical properties and the test values were compared with those of concrete from cement with natural gypsum. Compressive strength of concrete from cement produced with borogypsum was found to be higher than that of natural gypsum. Also, the setting time of cement with borogypsum was longer than that of the Portland cement.
Utilization of borogypsum as set retarder in Portland cement production
Boncukcuoglu, R. (Autor:in) / Yilmaz, M.T. (Autor:in) / Kocakerim, M.M. (Autor:in) / Tosunoglu, V. (Autor:in)
Cement and Concrete Research ; 32 ; 471-475
2002
5 Seiten, 15 Quellen
Aufsatz (Zeitschrift)
Englisch
Utilization of borogypsum as set retarder in Portland cement production
| Online Contents | 2002
Utilization of borogypsum as set retarder in Portland cement production
| British Library Online Contents | 2002
Utilization of weathered phosphogypsum as set retarder in Portland cement
| Online Contents | 2004
Utilization of weathered phosphogypsum as set retarder in Portland cement
| Tema Archiv | 2004