Characteristics of microcrack initiation in CuNiAl shape memory alloy
The mechanism of microcrack initiation in CuNiAl shape memory alloy was investigated through in situ tensile tests under optical microscopy, scanning electron microscopy and transmission electron microscopy. The results indicated that various martensite phases appeared first around a notch tip upon loading, and then microcracks initiated along the martensite/parent interface. The small martensite regions could transform back to the parent phase not only upon unloading but also upon loading or during crack propagation. There was no dislocation emission and motion before martensite formation. The slip bands formed after the crack had propagated a definite distance, and the microcracks nucleated and the cracks propagated either along the slip bands or the martensite/parent interface.
Characteristics of microcrack initiation in CuNiAl shape memory alloy
The mechanism of microcrack initiation in CuNiAl shape memory alloy was investigated through in situ tensile tests under optical microscopy, scanning electron microscopy and transmission electron microscopy. The results indicated that various martensite phases appeared first around a notch tip upon loading, and then microcracks initiated along the martensite/parent interface. The small martensite regions could transform back to the parent phase not only upon unloading but also upon loading or during crack propagation. There was no dislocation emission and motion before martensite formation. The slip bands formed after the crack had propagated a definite distance, and the microcracks nucleated and the cracks propagated either along the slip bands or the martensite/parent interface.
Characteristics of microcrack initiation in CuNiAl shape memory alloy
Lu, Y.H. (Autor:in) / Qiao, L.J. (Autor:in) / Chu, W.Y. (Autor:in)
Fatigue and Fracture of Engineering Materials and Structures ; 25 ; 509-518
2002
10 Seiten, 16 Quellen
Aufsatz (Zeitschrift)
Englisch
Characteristics of microcrack initiation in CuNiAl shape memory alloy
| British Library Online Contents | 2002
TEM observation of martensite reverse transformation during loading in CuNiAl shape memory alloys
| British Library Online Contents | 2001
Dynamic microcrack initiation in -iron
| British Library Online Contents | 1996
| British Library Online Contents | 2002
Microcrack initiation at tip of a rigid line inhomogeneity
| British Library Online Contents | 1996