Early-age deformation, drying shrinkage and thermal dilation in a new type of dental restorative material based on calcium aluminate cement
Dimensional changes during the first hour of hydration for small specimens of a dental material based on calcium aluminate cement (CAC) was examined. The study was conducted on specimens prepared in two different ways. First, intact tablets (three pieces per test) dipped in water were measured. Second, compacted specimens from four tablets were measured after 10 min of hydration. The dimensional changes were studied in both wet and dry conditions at 37 degree C and in a dry condition at 25 degree C. In the wet environment at 37 degree C no dimensional change of the samples was observed. At normal room humidity (RH 55%) at both temperatures, shrinkage of 0.35-0.40% was observed. For comparison to the early-age drying shrinkage, a study of the drying shrinkage in mature material, hydrated for 50 and 100 days, respectively, was conducted. Furthermore the thermal expansion coefficient was determined and found to be close to that of tooth substance.
Early-age deformation, drying shrinkage and thermal dilation in a new type of dental restorative material based on calcium aluminate cement
Dimensional changes during the first hour of hydration for small specimens of a dental material based on calcium aluminate cement (CAC) was examined. The study was conducted on specimens prepared in two different ways. First, intact tablets (three pieces per test) dipped in water were measured. Second, compacted specimens from four tablets were measured after 10 min of hydration. The dimensional changes were studied in both wet and dry conditions at 37 degree C and in a dry condition at 25 degree C. In the wet environment at 37 degree C no dimensional change of the samples was observed. At normal room humidity (RH 55%) at both temperatures, shrinkage of 0.35-0.40% was observed. For comparison to the early-age drying shrinkage, a study of the drying shrinkage in mature material, hydrated for 50 and 100 days, respectively, was conducted. Furthermore the thermal expansion coefficient was determined and found to be close to that of tooth substance.
Early-age deformation, drying shrinkage and thermal dilation in a new type of dental restorative material based on calcium aluminate cement
Kraft, Lars (Autor:in) / Engqvist, Hakan (Autor:in) / Hermansson, Leif (Autor:in)
Cement and Concrete Research ; 34 ; 439-446
2004
8 Seiten, 21 Quellen
Aufsatz (Zeitschrift)
Englisch
plastische Verformung , Schrumpfung , Hydratisieren , Wärmebehandlung , Maßbeständigkeit , mineralogische Zusammensetzung , Risseinleitung , Kompaktieren , Portlandzement , Wärmeausdehnung , Röntgenanalyse , Zementpaste , Tonerdeschmelzzement , zahnärztliches Behandlungsgerät , Dentalzement , Trockenschwindung
| British Library Online Contents | 2004
Shrinkage and Shrinkage Compensation in Binders Containing Calcium Aluminate Cement
| British Library Conference Proceedings | 2001
Shrinkage and shrinkage compensation in binders containing calcium aluminate cement
| Tema Archiv | 2001
Early-strength type aluminate cement based self-leveling material
| Europäisches Patentamt | 2015