Quantitative composition of ancient mortars from the Notre Dame Cathedral in Tournai (Belgium)
A combined micro- and macroscopical approach was implemented for the quantification of the main constituents in a set of 41 ancient mortar samples from Tournai (Belgium). The samples range in age from Roman to Romanesque. The microscopical study consisted of point counting on thin sections prepared from these mortars. If sufficiently large samples were available, Image Analysis on plane polished surfaces was used to quantify the larger objects (> 1 mm) as lime lumps or ceramics. In spite of possible uncertainties, general conclusions about these mortars could be drawn. The Roman and Palaeochristian mortars are all comparable in containing a considerable amount of ceramic fragments, whereas their presence was not systematic during later times. The binder/aggregate ratios varied from 0.4 to 2.3. Romanesque mortars seem to have a less variable binder to aggregate content compared to the older mortar samples.
Quantitative composition of ancient mortars from the Notre Dame Cathedral in Tournai (Belgium)
A combined micro- and macroscopical approach was implemented for the quantification of the main constituents in a set of 41 ancient mortar samples from Tournai (Belgium). The samples range in age from Roman to Romanesque. The microscopical study consisted of point counting on thin sections prepared from these mortars. If sufficiently large samples were available, Image Analysis on plane polished surfaces was used to quantify the larger objects (> 1 mm) as lime lumps or ceramics. In spite of possible uncertainties, general conclusions about these mortars could be drawn. The Roman and Palaeochristian mortars are all comparable in containing a considerable amount of ceramic fragments, whereas their presence was not systematic during later times. The binder/aggregate ratios varied from 0.4 to 2.3. Romanesque mortars seem to have a less variable binder to aggregate content compared to the older mortar samples.
Quantitative composition of ancient mortars from the Notre Dame Cathedral in Tournai (Belgium)
Mertens, G. (Autor:in) / Elsen, J. (Autor:in) / Brulet, R. (Autor:in) / Brutsaert, A. (Autor:in) / Deckers, M. (Autor:in)
Materials Characterization ; 60 ; 580-585
2009
6 Seiten, 25 Quellen
Aufsatz (Zeitschrift)
Englisch
Microscopical study of ancient mortars from Tournai (Belgium)
| Tema Archiv | 2004
Belgique: La restauration de la cathédrale Notre-Dame de Tournai
| DataCite | 2015
La sculpture romane de la cathédrale Notre-Dame de Tournai
| UB Braunschweig | 1971
Notre Dame Cathedral : Nine Centuries of History
| UB Braunschweig | 2021
Lead contamination risk near Notre-Dame cathedral
American Chemical Society | 2019