The role of alkali content of Portland cement on the expansion of concrete prisms containing reactive aggregates and supplementary cementing materials
This paper presents results covering the effects of alkali content of Portland cement (PC) on expansion of concrete containing reactive aggregates and supplementary cementing materials (SCM). The results showed that the alkali content of PC has a significant effect on expansion of concrete prisms with no SCM. When SCM is used, the expansion was found to be related to both the chemical composition of the SCM and, to a lesser extent, the alkali content of the PC. The concrete expansions were explained, at least partly, on the basis of the alkalinity of a pore solution extracted from hardened cement paste samples containing the same cementing blends. An empirical relation was developed correlating the chemical composition (Ca, Si and total Na2Oe) of the cementing blend (PC + SCM) and the alkalinity of the pore solution. Results from accelerated mortar bar test (ASTM C 1260) and a modified version thereof are also presented.
The role of alkali content of Portland cement on the expansion of concrete prisms containing reactive aggregates and supplementary cementing materials
This paper presents results covering the effects of alkali content of Portland cement (PC) on expansion of concrete containing reactive aggregates and supplementary cementing materials (SCM). The results showed that the alkali content of PC has a significant effect on expansion of concrete prisms with no SCM. When SCM is used, the expansion was found to be related to both the chemical composition of the SCM and, to a lesser extent, the alkali content of the PC. The concrete expansions were explained, at least partly, on the basis of the alkalinity of a pore solution extracted from hardened cement paste samples containing the same cementing blends. An empirical relation was developed correlating the chemical composition (Ca, Si and total Na2Oe) of the cementing blend (PC + SCM) and the alkalinity of the pore solution. Results from accelerated mortar bar test (ASTM C 1260) and a modified version thereof are also presented.
The role of alkali content of Portland cement on the expansion of concrete prisms containing reactive aggregates and supplementary cementing materials
Shehata, Medhat H. (Autor:in) / Thomas, Michael D.A. (Autor:in)
Cement and Concrete Research ; 40 ; 569-574
2010
6 Seiten, 17 Quellen
Aufsatz (Zeitschrift)
Englisch
| British Library Online Contents | 2010
Durability of Ikaline Portland Cement Concrete Made with Alkali-Reactive Aggregates
| British Library Conference Proceedings | 1997
Role of Supplementary Cementing Materials in Concrete
| British Library Conference Proceedings | 1995
Supplementary cementing materials in concrete
| TIBKAT | 2013