Refractory concretes uniaxial compression behaviour under high temperature testing conditions
Two refractory concretes with the same matrix composition, one based on andalusite aggregate and the other on bauxite aggregate, have been studied at temperatures ranging from room temperature to 1200 ° C maximal temperature. Samples dried at 110 ° C during 24 h to create dried standard specimens and others, fired at different temperatures, were subjected to several uniaxial compression test conditions conducted at various temperatures. The evolution of the materials' global behaviour from quasi-brittle to viscous was evidenced and correlated to their microstructure evolution. Loading/unloading, creep, and strain rate jump tests helped define the damageable and viscoplastic nature of the behaviour. The influence of the firing temperature and duration on the materials' behaviour is also reported and discussed. In conclusion, potential constitutive equations that are able to fit the material recorded behaviour are suggested.
Refractory concretes uniaxial compression behaviour under high temperature testing conditions
Two refractory concretes with the same matrix composition, one based on andalusite aggregate and the other on bauxite aggregate, have been studied at temperatures ranging from room temperature to 1200 ° C maximal temperature. Samples dried at 110 ° C during 24 h to create dried standard specimens and others, fired at different temperatures, were subjected to several uniaxial compression test conditions conducted at various temperatures. The evolution of the materials' global behaviour from quasi-brittle to viscous was evidenced and correlated to their microstructure evolution. Loading/unloading, creep, and strain rate jump tests helped define the damageable and viscoplastic nature of the behaviour. The influence of the firing temperature and duration on the materials' behaviour is also reported and discussed. In conclusion, potential constitutive equations that are able to fit the material recorded behaviour are suggested.
Refractory concretes uniaxial compression behaviour under high temperature testing conditions
Das uniaxiale Kompressionsverhalten von feuerfestem Beton unter Hochtemperatur-Testbedingungen
Ouedraogo, Evariste (Autor:in) / Roosefid, Mohsen (Autor:in) / Prompt, Nicolas (Autor:in) / Deteuf, Cyrille (Autor:in)
Journal of the European Ceramic Society ; 31 ; 2763-2774
2011
12 Seiten, 15 Bilder, 6 Tabellen, 30 Quellen
Aufsatz (Zeitschrift)
Englisch
feuerfester Beton , chemische Zusammensetzung , Andalusit , Bauxit , Aluminiumoxid , Siliciumoxid , Calciumoxid , Eisenoxid , Hochtemperaturversuch , Brenntemperatur , Druckversuch , Mikrogefüge , Kriechen (Werkstoff) , Verformungsgeschwindigkeit , Viskoplastizität , Haltezeit , mechanische Festigkeit
Thermomechanical behaviour of refractory dry-stacked masonry walls under uniaxial compression
| BASE | 2021
| Tema Archiv | 2001
Monolithic refractory concretes
| Engineering Index Backfile | 1932
Stress–strain model for normal- and light-weight concretes under uniaxial and triaxial compression
| Online Contents | 2014
Behaviour of steel-fibre-reinforced concretes under biaxial compression load
| Online Contents | 1995