Immobilisation of lead smelting slag within spent aluminate—fly ash based geopolymers
This study presents the solidification/stabilisation and immobilisation of lead smelting slag (LSS) by its incorporation in coal fly ash – blast furnace slag based geopolymers. It also explores the use of a spent aluminium etching solution (AES) as geopolymer activator instead of the commonly used silicate solutions. The compressive strength of the geopolymers produced with the AES was lower than when applying a K-silicate solution as activator (100 MPa versus 80 MPa after 28 days). Compressive strength was not affected when up to 10% of the FA was replaced by LSS. NEN 12457-4, TCLP, SPLP and NEN 7375 leaching tests indicated that mobile Pb from LSS was highly immobilised. The diffusion leaching test NEN 7375 revealed exceeding of the Dutch Soil Quality Regulation threshold limits only for Se and Sb. On the condition that the remaining excess leaching can be reduced by further refinement of the mixture recipes, the proposed process will have the potential of producing waste-based construction materials that may be applied under controlled conditions in specific situations.
Immobilisation of lead smelting slag within spent aluminate—fly ash based geopolymers
This study presents the solidification/stabilisation and immobilisation of lead smelting slag (LSS) by its incorporation in coal fly ash – blast furnace slag based geopolymers. It also explores the use of a spent aluminium etching solution (AES) as geopolymer activator instead of the commonly used silicate solutions. The compressive strength of the geopolymers produced with the AES was lower than when applying a K-silicate solution as activator (100 MPa versus 80 MPa after 28 days). Compressive strength was not affected when up to 10% of the FA was replaced by LSS. NEN 12457-4, TCLP, SPLP and NEN 7375 leaching tests indicated that mobile Pb from LSS was highly immobilised. The diffusion leaching test NEN 7375 revealed exceeding of the Dutch Soil Quality Regulation threshold limits only for Se and Sb. On the condition that the remaining excess leaching can be reduced by further refinement of the mixture recipes, the proposed process will have the potential of producing waste-based construction materials that may be applied under controlled conditions in specific situations.
Immobilisation of lead smelting slag within spent aluminate—fly ash based geopolymers
Ogundiran, M.B. (Autor:in) / Nugteren, H.W. (Autor:in) / Witkamp, G.J. (Autor:in)
Journal of Hazardous Materials ; 248-249 ; 29-36
2013
8 Seiten, 44 Quellen
Aufsatz (Zeitschrift)
Englisch
Geopolymer , Immobilisation , Aluminium , Kohlenasche , Silicate , Ätzen , Baumaterial , Inkorporierung , Diffusion , Druckfestigkeit , Hochofenschlacke , Tonerde , Aluminate , Flugasche
Effect of sulphate and nitrate anions on heavy metal immobilisation in ferronickel slag geopolymers
| Online Contents | 2013
Caesium Immobilisation in Hydrated Calcium-Silicate-Aluminate Systems
| British Library Online Contents | 1998
PAPERS - Caesium Immobilisation in Hydrated Calcium-Silicate-Aluminate Systems
| Online Contents | 1998
Synthesis and Characterisation of Slag Based Geopolymers
| British Library Online Contents | 2010
Highway engineering cement prepared based on lead smelting slag
| Europäisches Patentamt | 2023