Chloride Ion Penetrability of HPFRCC after Loading
Cracking is one of the most important factors in the serviceability as well as durability performance of concrete structures. Recently, it was recognized that a high performance fiber-reinforced cementitious composite (HPFRCC) provides a possible solution to this inherent problem of cracking by smearing one or several dominant cracks into many distributed microcracks. The purpose of the present study is to explore the ductility characteristics of HPFRCC. The permeability of HPFRCC after subjected to different load levels were measured to identify the effect of reduced cracking among the mixtures. It was confined that the permeability of proposed mixtures was lower than that without microfibers. This means that the proposed materials can reduce the crack width greatly at the same applied loads.
Chloride Ion Penetrability of HPFRCC after Loading
Cracking is one of the most important factors in the serviceability as well as durability performance of concrete structures. Recently, it was recognized that a high performance fiber-reinforced cementitious composite (HPFRCC) provides a possible solution to this inherent problem of cracking by smearing one or several dominant cracks into many distributed microcracks. The purpose of the present study is to explore the ductility characteristics of HPFRCC. The permeability of HPFRCC after subjected to different load levels were measured to identify the effect of reduced cracking among the mixtures. It was confined that the permeability of proposed mixtures was lower than that without microfibers. This means that the proposed materials can reduce the crack width greatly at the same applied loads.
Chloride Ion Penetrability of HPFRCC after Loading
Shin, Kyung-Joon (Autor:in)
2014
3 Seiten
Aufsatz (Konferenz)
Englisch
Chlorid , Hochtemperaturfaser , Mikrofaser , Mikroriss , Chloridion , Komposit , Duktilität , Rissbreite
Chloride Ion Penetrability of HPFRCC after Loading
| British Library Conference Proceedings | 2014
| British Library Conference Proceedings | 1996
| British Library Conference Proceedings | 2006
| Springer Verlag | 2022
RAPID CHLORIDE PENETRABILITY TEST: A NEW LOOK
| British Library Conference Proceedings | 2005