Threshold Chloride Levels for Localized Carbon Steel Corrosion in Simulated Concrete Pore Solutions Using Coupled Multielectrode Array Sensors
Threshold chloride levels for localized corrosion of carbon steel material have been studied in three types of simulated concrete pore solutions: sodium hydroxide-potassium hydroxide (NaOH-KOH) with pH 11.6, calcium hydroxide (Ca[OH]2) with pH 12.6, and sodium hydroxide-potassium hydroxide-calcium hydroxide (NaOH-KOH-Ca[OH]2) with pH 13.3. The nonuniform corrosion rates of carbon steel were measured with coupled multielectrode array sensors (CMAS) when the chloride concentration was changed from 0.0005 mol/L to 1 mol/L in each solution. Open-circuit potentials were also measured from the coupling joint of the CMAS probes and electrodes made of rebar specimens immersed in the simulated pore solutions to verify the results from the CMAS probes.
Threshold Chloride Levels for Localized Carbon Steel Corrosion in Simulated Concrete Pore Solutions Using Coupled Multielectrode Array Sensors
Threshold chloride levels for localized corrosion of carbon steel material have been studied in three types of simulated concrete pore solutions: sodium hydroxide-potassium hydroxide (NaOH-KOH) with pH 11.6, calcium hydroxide (Ca[OH]2) with pH 12.6, and sodium hydroxide-potassium hydroxide-calcium hydroxide (NaOH-KOH-Ca[OH]2) with pH 13.3. The nonuniform corrosion rates of carbon steel were measured with coupled multielectrode array sensors (CMAS) when the chloride concentration was changed from 0.0005 mol/L to 1 mol/L in each solution. Open-circuit potentials were also measured from the coupling joint of the CMAS probes and electrodes made of rebar specimens immersed in the simulated pore solutions to verify the results from the CMAS probes.
Threshold Chloride Levels for Localized Carbon Steel Corrosion in Simulated Concrete Pore Solutions Using Coupled Multielectrode Array Sensors
Yang, Lietai (Autor:in) / Chiang, Kuang-Tsan (Autor:in) / Yu, Hui (Autor:in) / Pabalan, Roberto T. (Autor:in) / Dasgupta, Biswajit (Autor:in) / Ibarra, Luis (Autor:in)
Corrosion, Houston ; 70 ; 850-857
2014
8 Seiten, Bilder, Tabellen, 27 Quellen
Aufsatz (Zeitschrift)
Englisch
| British Library Online Contents | 2014
| British Library Online Contents | 2010
An In-Situ Galvanically Coupled Multielectrode Array Sensor for Localized Corrosion
| British Library Online Contents | 2002
Online Monitoring of Undercoating Corrosion Using Coupled Multielectrode Sensors
| British Library Online Contents | 2005