Pozzolanic properties of flash-calcined kaolinite: A comparative study with soak-calcined products
Flash-calcination enables the dehydroxylation of powdered kaolinite clay within several tenths of a second, when traditional soak-calcinations require minutes at least. The pozzolanic properties of the metakaolin produced from two different kaolinites, using two different flash calciners, are shown to increase with the dehydroxylation rate, and rapidly to decrease at the occurence of recrystallisation for temperatures above 900 deg C. Flash-calcined products also revealed structural properties different from soak-calcined products. Two different lime reactivity tests were thus necessary to asses the pozzolanic properties of products: the compressive strengths of minicylinders of metakaolin and lime and water after solidification, and the Chapelle test. Processing flash-calcination in a temperature range that was determined, with a sufficient residence time, lead to metakaolins with lime reactivities similar or better than reactivities of standard metakaolin obtained by soak-calcination.
Pozzolanic properties of flash-calcined kaolinite: A comparative study with soak-calcined products
Flash-calcination enables the dehydroxylation of powdered kaolinite clay within several tenths of a second, when traditional soak-calcinations require minutes at least. The pozzolanic properties of the metakaolin produced from two different kaolinites, using two different flash calciners, are shown to increase with the dehydroxylation rate, and rapidly to decrease at the occurence of recrystallisation for temperatures above 900 deg C. Flash-calcined products also revealed structural properties different from soak-calcined products. Two different lime reactivity tests were thus necessary to asses the pozzolanic properties of products: the compressive strengths of minicylinders of metakaolin and lime and water after solidification, and the Chapelle test. Processing flash-calcination in a temperature range that was determined, with a sufficient residence time, lead to metakaolins with lime reactivities similar or better than reactivities of standard metakaolin obtained by soak-calcination.
Pozzolanic properties of flash-calcined kaolinite: A comparative study with soak-calcined products
Puzzolanische Eigenschaften von schnellcalciniertem Kaolinit: Ein Vergleich mit langsam calcinierten Produkten
Salvador, S. (Autor:in)
Cement and Concrete Research ; 25 ; 102-112
1995
11 Seiten, 7 Bilder, 2 Tabellen, 8 Quellen
Aufsatz (Zeitschrift)
Englisch
Pozzolanic Properties of Flash-Calcined Kaolinite: A Comparative Study with Soak-Calcined Products
| Online Contents | 1995
Pozzolanic Properties of Flash-Calcined Kaolinite: A Comparative Study with Soak-Calcined Products
| British Library Online Contents | 1995
Experimental investigation and comparison of soak and flash calcined kaolinite and montmorillonite
| Elsevier | 2025
Comparison of the Pozzolanic Reactivity for Flash and Soak Calcined Clays in Portland Cement Blends
| Springer Verlag | 2015