Mercury porosimetry of hardened cement pastes
Mercury porosimetry was performed on 92 hardened cement paste specimens of water/cement (w/c) ratios 0.3, 0.4, 0.5, 0.6, and 0.7 and curing times of 1, 3, 7, 14, 28, and 56 days. This paper presents the experimental techniques, results, and their possible implications with respect to pore connectivity. As expected, longer curing times and lower w/c ratios resulted in smaller indicated total porosities and smaller threshold pore widths. Longer curing times and higher w/c ratios resulted in greater degrees of hydration. In most of the mercury intrusion results, two peaks could be observed in the differential curves that were identified as the 'initial' and 'rounded' peaks. The initial peak may correspond to the intrusion of mercury through a connected capillary network, while the rounded peak may correspond to the crushing of interposed hydration products.
Mercury porosimetry of hardened cement pastes
Mercury porosimetry was performed on 92 hardened cement paste specimens of water/cement (w/c) ratios 0.3, 0.4, 0.5, 0.6, and 0.7 and curing times of 1, 3, 7, 14, 28, and 56 days. This paper presents the experimental techniques, results, and their possible implications with respect to pore connectivity. As expected, longer curing times and lower w/c ratios resulted in smaller indicated total porosities and smaller threshold pore widths. Longer curing times and higher w/c ratios resulted in greater degrees of hydration. In most of the mercury intrusion results, two peaks could be observed in the differential curves that were identified as the 'initial' and 'rounded' peaks. The initial peak may correspond to the intrusion of mercury through a connected capillary network, while the rounded peak may correspond to the crushing of interposed hydration products.
Mercury porosimetry of hardened cement pastes
Cook, R.A. (Autor:in) / Hover, K.C. (Autor:in)
Cement and Concrete Research ; 29 ; 933-943
1999
11 Seiten, 38 Quellen
Aufsatz (Zeitschrift)
Englisch
PAPERS - Mercury porosimetry of hardened cement pastes
| Online Contents | 1999
| British Library Online Contents | 1999
| British Library Conference Proceedings | 1996
Mercury intrusion porosimetry and hierarchical structure of cement pastes
| British Library Online Contents | 2000
Porosity of hardened Portland cement pastes
| Engineering Index Backfile | 1956