Study of Fly Ash Concrete Exposed to Elevated Temperature
The ability to improve the tendency of hardened concrete in compression at elevated temperature was studied. Five mixes of fly ash were cast with a replacement amount of 0%, 10%, 20%, 30%, and 40% by cement mass. They were exposed to 400°C and held for 2 hours after water curing. The specimens have been cooled down to room temperature and then undergo a compressive test. This research aims to study the physical and mechanical properties of fly ash concrete after being exposed to elevated temperatures. A digital microscope was used to analyse the formation mechanism of microstructure in concrete. Fly ash was used to produce high fire resistance concrete with 100 mm x 100 mm x 100 mm concrete cube. Sample 4 with 30% fly ash has the highest compressive strength with 26 MPa after 28 days and 21 MPa after exposed to 400°C. The results show that concrete containing a high amount of fly ash has several improvements when exposed to elevated temperature. The concrete specimens were used to validate an interfacial transition zone (ITZ) in concrete. The microstructure features were discussed concerning their influence on the strength development of concrete.
Study of Fly Ash Concrete Exposed to Elevated Temperature
The ability to improve the tendency of hardened concrete in compression at elevated temperature was studied. Five mixes of fly ash were cast with a replacement amount of 0%, 10%, 20%, 30%, and 40% by cement mass. They were exposed to 400°C and held for 2 hours after water curing. The specimens have been cooled down to room temperature and then undergo a compressive test. This research aims to study the physical and mechanical properties of fly ash concrete after being exposed to elevated temperatures. A digital microscope was used to analyse the formation mechanism of microstructure in concrete. Fly ash was used to produce high fire resistance concrete with 100 mm x 100 mm x 100 mm concrete cube. Sample 4 with 30% fly ash has the highest compressive strength with 26 MPa after 28 days and 21 MPa after exposed to 400°C. The results show that concrete containing a high amount of fly ash has several improvements when exposed to elevated temperature. The concrete specimens were used to validate an interfacial transition zone (ITZ) in concrete. The microstructure features were discussed concerning their influence on the strength development of concrete.
Study of Fly Ash Concrete Exposed to Elevated Temperature
Key Engineering Materials ; 908 ; 645-650
28.02.2022
6 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Residual Fracture Toughness of Concrete Exposed to Elevated Temperature
| Online Contents | 1998
High-strength concrete exposed to elevated temperature - spalling and protection
| Tema Archiv | 2003
HIGH-STRENGTH CONCRETE EXPOSED TO ELEVATED TEMPERATURE-SPALLING AND PROTECTION
| British Library Conference Proceedings | 2003
Experimental Studies on Brick Powder Replaced Concrete Exposed to Elevated Temperature
| Springer Verlag | 2019