Finite Element Analysis for Concrete Damage under Freeze-Thaw Action
Freeze-thaw damage is one of the most representative damages in concrete durability. Commonly, freezing and thawing tests are conducted to investigate the freeze-thaw resistance of concrete, and the loss of dynamic modulus of concrete is regarded as the failure criterion. However, the research on the evolution of concrete strength during the damage process is still not enough when subjected to freezing and thawing. In this study, the concrete freeze-thaw deterioration was considered as isotropic elastic damage, and relative variation functions of dynamic modulus and Poisson’s ratio with freeze-thaw cycles were set up. Based on damage mechanics, the Ottosen failure surface model with four parameters was established to indicate the relationship between the concrete freeze-thaw failure surface and freeze-thaw cycles. Then the four-parameter failure surface model was set into ADINA finite element software program for secondary development to investigate the strength properties of concrete component under freeze-thaw action. The relationship between load and deflection of concrete was analyzed and simulated after 0, 25 and 50 freeze-thaw cycles. The simulated and experimental results are basically identical, which demonstrates that this finite element simulation is a feasible way to analyze and evaluate the performance of concrete structures in cold regions.
Finite Element Analysis for Concrete Damage under Freeze-Thaw Action
Freeze-thaw damage is one of the most representative damages in concrete durability. Commonly, freezing and thawing tests are conducted to investigate the freeze-thaw resistance of concrete, and the loss of dynamic modulus of concrete is regarded as the failure criterion. However, the research on the evolution of concrete strength during the damage process is still not enough when subjected to freezing and thawing. In this study, the concrete freeze-thaw deterioration was considered as isotropic elastic damage, and relative variation functions of dynamic modulus and Poisson’s ratio with freeze-thaw cycles were set up. Based on damage mechanics, the Ottosen failure surface model with four parameters was established to indicate the relationship between the concrete freeze-thaw failure surface and freeze-thaw cycles. Then the four-parameter failure surface model was set into ADINA finite element software program for secondary development to investigate the strength properties of concrete component under freeze-thaw action. The relationship between load and deflection of concrete was analyzed and simulated after 0, 25 and 50 freeze-thaw cycles. The simulated and experimental results are basically identical, which demonstrates that this finite element simulation is a feasible way to analyze and evaluate the performance of concrete structures in cold regions.
Finite Element Analysis for Concrete Damage under Freeze-Thaw Action
Key Engineering Materials ; 417-418 ; 133-136
08.10.2009
4 pages
Aufsatz (Zeitschrift)
Elektronische Ressource
Englisch
Finite Element Analysis for Concrete Damage under Freeze-Thaw Action
| British Library Online Contents | 2010
Aging Mechanism of Dam Concrete under the Action of Freeze-Thaw Damage
| Trans Tech Publications | 2014
Aging Mechanism of Dam Concrete under the Action of Freeze-Thaw Damage
| British Library Conference Proceedings | 2014
Probabilistic damage modeling and service-life prediction of concrete under freeze–thaw action
| Online Contents | 2014
Study on Non-Local Damage Constitutive Model of Concrete under Freeze-Thaw Action
| British Library Online Contents | 2011